Reduction of Hexavalent Chromium by Viable Cells of Chromium Resistant Bacteria Isolated from Chromite Mining Environment

Dey, Satarupa; Pandit, Baishali; Paul, A. K.

doi:https://doi.org/10.1155/2014/941341

Journal of Mining

On this page

Abstract Introduction Materials and Methods Results and Discussion Conclusion References Copyright Related Articles

Research Article | Open Access

Volume 2014 | Article ID 941341 | https://doi.org/10.1155/2014/941341

Reduction of Hexavalent Chromium by Viable Cells of Chromium Resistant Bacteria Isolated from Chromite Mining Environment

Satarupa Dey,¹Baishali Pandit,¹and A. K. Paul¹

Academic Editor: Yong Sik Ok

Received27 Apr 2014

Revised10 Jul 2014

Accepted15 Jul 2014

Published10 Aug 2014

Abstract

Environmental contamination of hexavalent chromium [Cr(VI)] is of serious concern for its toxicity as well as mutagenic and carcinogenic effects. Bacterial chromate reduction is a cost-effective technology for detoxification as well as removal of Cr(VI) from polluted environment. Chromium resistant and reducing bacteria, belonging to Arthrobacter, Pseudomonas, and Corynebacterium isolated from chromite mine overburden and seepage samples of Orissa, India, were found to tolerate 12–18 mM Cr(VI) during growth. Viable cells of these isolates were also capable of growing and reducing 100 μM Cr(VI) quite efficiently in Vogel Bonner (V.B.) broth under batch cultivation. Freshly grown cells of the most potent isolate, Arthrobacter SUK 1201, reduced 100 μM Cr(VI) in 48 h. Reduction potential of SUK 1201 cells decreased with increase in Cr(VI) concentration but increased with increase in cell density and attained its maximum at 10¹⁰ cells/mL. Chromate reducing efficiency of SUK 1201 was promoted in the presence of glucose and glycerol while the highest reduction was at pH 7.0 and 25°C. The reduction process was inhibited by divalent cations Ni, Co, and Cd, but not by Cu. Similarly, carbonyl cyanide m-chlorophenylhydrazone, N,N,-Di cyclohexyl carbodiimide, sodium azide, and sodium fluoride were inhibitory to chromate reduction, while 2,4 dinitrophenol promoted the process. Cells permeabilized by toluene increased the efficiency of Cr(VI) reduction and, thereby, indicate that Arthrobacter sp. SUK 1201, indigenous to chromite mining environment, could be used as an ideal tool for chromium bioremediation.

1. Introduction

Mining activities in and around chromite mines, in general, lead to the generation of huge amount of overburden material as well as accumulation of mine seepage waters, which are the main sources of chromium pollution of inland fresh water and farm lands in the vicinity of the mining sites. The chromite mining in the vast area of Orissa, India, is no exception to this generalization [1, 2].

In humans, several health hazards are associated with continuous exposure to Cr(VI). This is mainly because of its carcinogenic as well as mutagenic properties. Workers employed in areas highly contaminated with chromium suffer from nasal irritation and ulceration, skin irritation, eardrum perforation, lung carcinoma [3, 4], bronchial asthma, kidney necrosis, and allergic reactions in the skin. At higher level, chromium is also found to cause oxidative damage to cell membrane, alteration of enzyme specificity, and structural deformation in DNA [5].

Conventional methods used for removal of Cr(VI) comprised of chemical reduction followed by precipitation through adjustment of pH, ion exchange, and adsorption generate large quantities of solid sludge for disposal and are expensive and lack specificity [6]. Bioremediation, on the other hand, is an ecofriendly alternative for detoxification and removal of Cr-pollutants which uses indigenous microbiota [7]. Microbial reduction of hexavalent chromium has attracted increased interest, as this process not only relieves the toxicity of chromium but also leads to the precipitation at near-neutral pH for subsequent physical removal [8]. Chromium resistant and reducing bacteria isolated from chromium polluted environments such as tannery effluent and chromite mining environments have played a key role in chromium bioremediation [9–13].

During the course of our survey of chromium resistant and reducing bacteria, four efficient chromite reducing strains, namely, Arthrobacter sp. SUK 1201 (MTCC 8728, GenBank accession number JQ 312665), Arthrobacter sp. SUK 1205 (MTCC 8731, GenBank accession number JQ 312666), Pseudomonas putida SKPD 1202 (MTCC 8729), and Corynebacterium paurometabolum SKPD 1204 (MTCC 8730) were isolated from the chromite mining environment of Orissa, India [12–14]. The main objective of the present study was to determine their chromium tolerance along with reduction of Cr(VI) by viable cells of these selected bacterial isolates in Vogel Bonner (V. B.) broth. Further, attempts have also been made to optimize the cultural conditions for Cr(VI) reduction by viable cells of the isolate Arthrobacter sp. SUK 1201 in V. B. broth under batch culture and to assess the ability of this isolate as an ideal tool for hexavalent chromium bioremediation.

2. Materials and Methods

2.1. Source and Maintenance of Bacterial Cultures

Four chromate reducing bacterial strains, namely, Arthrobacter sp. SUK 1201 (MTCC 8728, GenBank accession number JQ 312665), Arthrobacter sp. SUK 1205 (MTCC 8731, GenBank accession number JQ 312666), Pseudomonas putida SKPD 1202 (MTCC 8729), and Corynebacterium paurometabolum SKPD 1204 (MTCC 8730) isolated from chromite mining environment of Orissa, India [12–14], were used in this study. Arthrobacter sp. SUK 1201 and Arthrobacter sp. SUK 1205 were isolated from chromite mine overburden samples, whereas Pseudomonas putida SKPD 1202 and Corynebacterium paurometabolum SKPD 1204 were isolated from chromite mine seepage samples. For maintenance, the bacterial strains were grown on slopes of peptone yeast extract glucose (PYEG) agar medium supplemented with 2 mM Cr(VI) [15]. The medium contained (g/L) peptone, 10.0; yeast extract, 5.0; glucose, 3.0, and agar agar, 20.0 (pH 7.0). Overnight grown cultures were stored at 4°C for future use.

2.2. Chromate Tolerance

Bacterial tolerance to hexavalent chromium was evaluated following broth dilution method of Calomiris et al. [16]. V. B. broth supplemented with different concentrations of Cr(VI) (2–20 mM) was inoculated with overnight grown cultures and incubated at 35°C for 4 days under continuous shaking (120 rpm) in a rotary shaker. Tolerance to Cr(VI) was calculated by determining the relative growth of the isolates with respect to the growth in control [Cr(VI)-free medium], which was considered as 100. Growth of the isolates was measured by determining the optical density at 540 nm.

2.3. Preparation of Cell Mass

Cell mass for chromate reduction studies was obtained by growing the isolates in PYEG medium at 35°C for 24 h under continuous shaking at 120 rpm. The cell mass of the isolates was harvested aseptically by centrifugation (10,000 ) at 4°C for 10 min, washed 2-3 times with sterile ice cold Tris buffer (pH 7.0), and suspended in the same buffer following the method of Wang and Xiao [15]. The cell mass was adjusted to a final cell density of 10⁹ cells/mL of reduction medium and used for reduction studies. Viability of cells was determined by dilution and plating of the cell suspension on PYEG agar plates. During the course of hexavalent chromium reduction, changes of cell numbers in the reduction medium were determined by counting the total number of cells/mL by using a haemocytometer (Neubauer, Fein-Optik Jena, Germany) and a phase contrast microscope (Zeiss Winkel Model number 148786, Germany).

2.4. Chromate Reduction Assay

Reduction of Cr(VI) by freshly grown cells of the selected bacterial strains was determined in V. B. broth. Vogel Bonner broth was made up of 2.0% sterile stock solution of V. B. concentrate. The V. B. concentrate contained (g/L) K₂HPO₄, 500.0; Na(NH₄)HPO₄4H₂O, 175.0; citric acid, 100.0; MgSO₄7H₂O, 10.0, and 2.0% of 25% D-glucose 20.0 (pH 7.0) [15]. Medium (20 mL/100 mL flask) was supplemented with separately sterile solution of 100 μM Cr(VI). Flasks were inoculated with viable cells at a density of 10⁹cells/mL under aseptic condition and incubated at 25°C under continuous shaking (120 rpm). The cell number and the viability of cells were determined following the same procedure as described in Section 2.3. Control (without cells) and autoclaved cells were also used for each Cr(VI)-reduction assay to monitor any abiotic Cr(VI)-reduction and biosorption of Cr(VI) by the cell mass.

Reduction of chromium was estimated by measuring the decrease of Cr(VI) contents in the reaction mixture following 1,5-diphenylcarbazide method [17]. Changes in the population of viable cells, if any, during the process of Cr(VI) reduction were also monitored by dilution and plating method on PYEG agar.

2.5. Effect of Electron Donors on Chromate Reduction

Chromate reduction by viable cells of Arthrobacter sp. SUK 1201 was studied in presence of various electron donors, such as glucose, glycine, glycerol, acetate, peptone, sucrose, propionate, yeast extract, benzoate, and tryptone. The reduction medium (20 mL of V. B. broth/100 mL) was supplemented with sterile 100 μM Cr(VI) along with the electron donors at 0.1% (w/v). Conditions of incubation, measurement of growth, harvesting of cells, and estimation of residual hexavalent chromium in the reduction medium were the same as described in earlier sections.

2.6. Effect of Temperature and pH on Chromate Reduction

Effect of different temperature (20°–40°C) and pH (6.0–8.0) on the Cr(VI) reducing capability of viable cells of Arthrobacter sp. SUK 1201 was determined. The effect of pH was determined at a wide range (pH 6.0–8.0) using citrate, phosphate, and Tris-HCl buffers with overlapping pH range. Chromate concentration, cell density/mL, and incubation conditions were the same as described earlier.

2.7. Effect of Additional Metal Ions on Chromate Reduction

Chromate reduction by Arthrobacter sp. SUK 1201 cells was studied in presence of additional metal ions such as Mn(II), Co(II), Zn(II), Cu(II), and Ni(II). The metals were used as chloride salts, sterilized separately, and added to V. B. broth at equimolar (100 μM) level of Cr(VI). Other experimental conditions were the same as described above.

2.8. Effect of Inhibitors on Chromate Reduction

The effect of metabolic inhibitors on chromate reduction by viable cells of Arthrobacter sp. SUK 1201 was investigated using the ATPase inhibitor N,N,-Di cyclohexyl carbodiimide (DCC), protonophore carbonyl cyanide m-chlorophenylhydrazone (CCCP), enolase inhibitor sodium fluoride, artificial electron acceptor sodium azide, and 2,4 dinitrophenol (DNP). The inhibitors were separately sterilized and added to the reduction medium at equimolar concentration. Other experimental conditions were the same as described previously.

2.9. Reduction by Permeabilized Cells

Permeabilized cells were obtained by harvesting overnight grown cultures of Arthrobacter sp. SUK 1201, washed, and suspended in sterile Tris-HCl buffer (pH 7.0). Toluene, Triton X100, and Tween 80 were added to the cell suspension at 0.1% (v/v) concentration and vortexed for 10 minutes to permeabilize the cells. Chromate reduction assay with these permeabilized cells was performed in the same way as described above, while the untreated cells were used as control.

2.10. Statistical Analysis

All experiments were carried out in triplicate and results represent mean ± standard error.

3. Results and Discussion

Biotransformation of highly toxic and mutagenic hexavalent chromium [18] to relatively nontoxic trivalent Cr(III) form by chromate reducing bacteria offers an economical as well as ecofriendly option for chromium bioremediation. Four chromate reducing bacterial strains, namely, Arthrobacter sp. SUK, Arthrobacter sp. SUK 1205, Pseudomonas putida SKPD 1202, and Corynebacterium paurometabolum SKPD 1204 were previously isolated and reported from chromite mine overburden and mine seepage samples and found to reduce chromate during growth under aerobic conditions [12, 14].

3.1. Chromate Tolerance

Chromium tolerance of the isolates as evident from the relative growth of the isolates in Cr(VI) supplemented media is represented in Figure 1. A significant difference in the growth of the selected isolates was recorded in V. B. broth supplemented with 2–20 mM of Cr(VI). As the concentration of chromium increased, the growth of the bacterial isolates decreased. The growth of the isolates was reduced to almost 50% of the control [without Cr(VI) ] at hexavalent chromium concentration of 2 mM and was strongly inhibited at 12 mM Cr(VI). Isolates Arthrobacter sp. SUK 1201 and Corynebacterium paurometabolum SKPD 1204 tolerated up to 18 and 16 mM Cr(VI), respectively, showing nearly 20% growth relative to control.

3.2. Chromate Reduction by Viable Cells

Reduction of Cr(VI) by viable cells has been studied using a variety of microorganisms [10, 19] in both aerobic [20, 21] and anaerobic conditions [22, 23]. Monitoring of Cr(VI) reduction and growth of the suspended cells of all 4 bacterial strains, namely, SUK 1201, SUK 1205, SKPD 1202, and SKPD 1204 (Figure 2) indicates that the strains were very much resistant to Cr(VI) and reduced it effectively. Both Arthrobacter isolates, that is, SUK 1201 and SUK 1205, completely reduced 100 μM Cr(VI) in 48 h. Reduction of Cr(VI) was accomplished by gradual discolouration of the medium but the pattern of increase in cell number/mL of medium was different for the different strains. In SUK 1201, cell number increased till 40 h of incubation and was followed by a decline, while in SUK 1205, there was a gradual increase till 48 h of incubation. The other two isolates, Pseudomonas putida SKPD 1202 and Corynebacterium paurometabolum SKPD 1204, could reduce about 90% of 100 μM Cr(VI) during the same period of incubation. Therefore, based on the limit of Cr(VI) tolerance (18 mM) and the efficiency of chromate reduction [100 μM Cr(VI) in 48 h], Arthrobacter sp. SUK 1201 was selected for further studies.

3.3. Effect of Initial Cr(VI) Concentration

The effect of different initial Cr(VI) concentrations (50–800 μM) were tested on Cr(VI) reducing ability of Arthrobacter sp. SUK 1201. The results presented in Table 1 showed that cells of SUK 1201 completely reduced 50 and 100 μM Cr(VI) 24 h and in 48 h respectively. The other concentrations of Cr(VI) were also significantly reduced within 48 h and about 75% of total Cr(VI) was reduced at the highest concentration (800 μM) tested. Likewise, chromate reduction by viable cells of different chromate reducing bacterial isolates was found to be influenced by the initial Cr(VI) concentration [11, 24, 25]. The present study showed that complete reduction failed to occur at higher initial Cr(VI) concentration (Table 1) which also corroborates the findings of several others [26, 27] with Arthrobacter sp. Such decrease in chromate reduction capability with the increasing concentration of initial Cr(VI) might be due to toxicity of chromium to viable whole cells.

3.4. Effect of Initial Cell Density

Reduction of Cr(VI) increased proportionally with increase in cell density ranging from 10⁶ to 10¹⁰ cells/mL (Table 2). Arthrobacter sp. SUK 1201 cells reduced 100 μM Cr(VI) in 48 h when the initial cell concentration was maintained at 10⁹ cells/mL; however, with 10 fold increase in cell density, 100 μM Cr(VI) was completely reduced in 30 h. Increase in cell density stimulated Cr(VI) reduction process (Table 2) as has been reported with Bacillus sphaericus AND 303 [28], Pseudomonas CRB5 [29], Ochrobactrum intermedium SDCr-5 [30], Lysinibacillus fusiformis ZC1 [25], and Arthrobacter sp. SUK 1205 [27].

3.5. Effect of Different Electron Donors

The effect of different electron donors on Cr(VI) reduction by Arthrobacter sp. SUK 1201 cells was studied. The electron donors include glucose, glycine, glycerol, acetate, peptone, sucrose, propionate, yeast extract, benzoate, and tryptone, which were added at 0.1% concentration to the reaction mixture. Cells of SUK 1201 completely reduced 100 μM Cr(VI) in 12 h when glucose was used as the electron donor (Figure 3). Glycerol, acetate, and peptone as electron donors could have completely reduced the added Cr(VI) in 24 h, while glycine and yeast extract appeared to be less efficient electron donors for reducing Cr(VI). Likewise, chromate reducing organisms are reported to utilize a variety of organic compounds as electron donors for Cr(VI) reduction [27, 31]. Whole cells of Arthrobacter sp. SUK 1205 [26], Ochrobactrum sp. strain CSCr-3 [24], and Bacillus cereus [32] were also found to utilize glucose as electron donor for efficient chromate reduction.

Figure 3

Effect of electron donor supplementation on Cr(VI) reduction by viable cells of Arthrobacter sp. SUK 1201. [Cr(VI)reduction was carried out in V. B. broth containing 100 μM Cr(VI). The initial cell density was maintained at 10⁹cells/mL. The electron donor was present at 0.1% w/v level, and 0.01% w/v glucose was present in control set. Incubation: 48 h at 25°C under continuous shaking (120 rpm). Residual Cr(VI) was measured by diphenylcarbazide method. Results represent mean of triplicate experiments ± standard error].

3.6. Effect of Temperature and pH

Environmental factors, such as temperature and pH were found to influence the chromate reducing potential of the viable cells of SUK 1201 (Figures 4(a) and 4(b)) as these two factors, in general, regulate the metabolic activities of the cells. The optimum temperature and pH for Cr(VI) reduction were 25°C (Figure 4(a)) and 7.0 (Figure 4(b)), respectively. On either side of the pH and temperature scale, the reduction capability of the cells was impaired. Optimum temperature was found to range between 35°C–37°C with Ochrobactrum intermedium Rb-2 [33], Ochrobactrum sp. CSCr-3 [24], O. intermedium SDCr-5 [30], and Nesterenkonia sp. MF2 [34]. It is presumed that deviation of these factors from their optima might alter the chromate reductase activity possibly due to change in the conformation and/or ionization of the enzyme [35].

(a)

(b)

Figure 4

Effect of temperature (a) and pH (b) on chromate reduction by viable cells of Arthrobacter sp. SUK 1201. [Cr(VI)reduction was carried out in V. B. broth containing 100 μM Cr(VI). The initial cell density was maintained at 10⁹cells/mL. The initial temperature was maintained from 20–40°C and pH of the reaction medium was maintained in the range of pH 6.0 to 8.0. Residual Cr(VI) was measured by diphenylcarbazide method. Results represent mean of triplicate experiments ± standard error].

3.7. Effect of Metal Ions

The process of chromate reduction is adversely affected by the presence of additional metal ions possibly due to metal toxicity and inhibition of the Cr(VI) reduction process [36]. Chromate reduction by viable cells of Arthrobacter sp. SUK 1201 was in general negatively affected when the reduction medium was supplemented with different heavy metals such as Ni(II), Zn(II), Mn(II), and Co(II) at equimolecular concentration. As compared to control, presence of Ni(II), Zn(II), Mn(II), and Co(II) showed nearly 66%, 74%, 60%, and 64% reduction, respectively (Table 3). However, Cr(VI) reducing capability of the isolate was enhanced when Cu(II) was present in the medium along with Cr(VI). Such stimulatory effect of Cu(II) on Cr(VI) reduction activity has also been reported for Cr(VI)-reduction by Bacillus sp. ES 29 [7], O. intermedium strain SDCr-5 [30], Ochrobactrum sp. strain CSCr-3 [24], Amphibacillus sp. KSUCr3, Bacillus sp. KSUCr9a [37, 38], and Arthrobacter sp. SUK 1205 [27]. The function of Cu(II) is either related to electron transport protection or to act as an electron redox centre, in some cases, as a shuttle for electrons between protein subunits [7, 24, 39].

3.8. Effect of Inhibitors

Inhibitors of different type such as sodium azide (NaN₃), sodium fluoride (NaF), 2,4-dinitrophenol (DNP), carbonyl cyanide-m-chlorophenyl hydrazone (CCCP), and N,N,-Di cyclohexyl carbodiimide (DCC) (DCC) were used at equimolecular concentration to assess their influence on chromate reduction by viable cells of Arthrobacter SUK 1201. The influence of DNP was exceptionally different from the rest. In presence of DNP, cells of SUK 1201 could reduce nearly 80% of the 100 μM Cr(VI) as compared to 50% reduction in the control in 24 h of incubation (Figure 5). On prolonged incubation (48 h), control and DNP treated cells completely reduced the 100 μM of Cr(VI). Such promoting effect of DNP has also been reported in Burkholderia cepacia [40] and Staphylococcus gallinarum [11] and Arthrobacter sp. SUK 1205 [27]. Further, it has been pointed out that DNP, being an uncoupler, might have accelerated the respiratory chain linked electron transport mechanism [40]. Amongst the rest, DCC was most inhibitory showing only 53% Cr(VI) reduction and was followed by NaN₃ and NaF (57% in both) and CCCP (71%). These inhibitors are known to inhibit the activity of cytochrome oxidase and enolase [9], disrupt chemiosmotic gradient, and inhibit the ATPase activity.

Figure 5

Effect of inhibitor on chromate reduction by viable cells of Arthrobacter sp. SUK 1201. [Cr(VI) reduction was carried out in V. B. broth containing 100 μM Cr(VI). The initial cell density was maintained at 10⁹cells/mL. Incubation: 48 h at 25°C under continuous shaking (120 rpm). All inhibitors were sterilized separately and added to V. B. broth at equimolar (100 μM) level of Cr(VI). Residual Cr(VI) was estimated by usual diphenylcarbazide method. Results represent mean of triplicate experiments ± standard error].

3.9. Effect of Permeabilized Cells on Reduction

Freshly grown cells of Arthrobacter sp. SUK 1201 were permeabilized in presence of triton, toluene, and tween 80 and used for chromate reduction studies. Efficient reduction of hexavalent chromium was achieved with toluene treated cells in 24 h and was followed by cells treated with triton and tween 80 which took 42 h to reduce the total Cr(VI) in the media as against 48 h in the control (Figure 6). Permeabilized cells of Arthrobacter sp. SUK 1201 as induced by triton X-100, toluene, and tween 80 have enhanced the reduction of chromate (Figure 6), which might indicate that the Cr(VI) reduction is mediated by soluble protein of the cell [6]. Similar enhancement in Cr(VI) reduction rate was observed with Providencia sp. [41].

4. Conclusion

The optimization of different conditions of Cr(VI) reduction by viable cells of Arthrobacter SUK 1201 has categorically established the biotechnological potential of this bacterial strain for transformation of highly toxic and mutagenic Cr(VI) to less toxic Cr(III) and, thus, could be used in detoxification of chromium pollutants.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.

Acknowledgment

The authors acknowledge the financial support from the Department of Biotechnology, Ministry of Science and Technology, Government of India vide Sanction no. BT/PR/5766/NDB/51/061/2005.

References

R. K. Tiwary, R. Dhakate, V. Ananda Rao, and V. S. Singh, “Assessment and prediction of contaminant migration in ground water from chromite waste dump,” Environmental Geology, vol. 48, no. 4-5, pp. 420–429, 2005.
View at: Publisher Site | Google Scholar
G. Godgul and K. C. Sahu, “Chromium contamination from chromite mine,” Environmental Geology, vol. 25, no. 4, pp. 251–257, 1995.
View at: Publisher Site | Google Scholar
H. J. Gibb, P. S. Lee, P. F. Pinsky, and B. C. Rooney, “Lung cancer among workers in chromium chemical production,” American Journal of Industrial Medicine, vol. 38, pp. 115–126, 2000.
View at: Google Scholar
H. J. Gibb, P. S. Lee, P. F. Pinsky, and B. C. Rooney, “Clinical findings of irritation among chromium chemical production workers,” American Journal of Industrial Medicine, vol. 38, no. 2, pp. 127–131, 2000.
View at: Google Scholar
M. R. Bruins, S. Kapil, and F. W. Oechme, “Microbial resistance to metallothionein in the environment,” Journal of Environmental Microbiology, vol. 45, no. 1, pp. 351–364, 2000.
View at: Google Scholar
U. Thacker and D. Madamwar, “Reduction of toxic chromium and partial localization of chromium reductase activity in bacterial isolate DM1,” World Journal of Microbiology and Biotechnology, vol. 21, no. 6-7, pp. 891–899, 2005.
View at: Publisher Site | Google Scholar
F. A. O. Camargo, B. C. Okeke, F. M. Bento, and W. T. Frankenberger, “In vitro reduction of hexavalent chromium by a cell-free extract of Bacillus sp. ES 29 stimulated by Cu²⁺,” Applied Microbiology and Biotechnology, vol. 62, no. 5-6, pp. 569–573, 2003.
View at: Publisher Site | Google Scholar
K. H. Cheung and J. D. Gu, “Reduction of chromate (CrO₄^2-) by an enrichment consortium and an isolate of marine sulfate-reducing bacteria,” Chemosphere, vol. 52, no. 9, pp. 1523–1529, 2003.
View at: Publisher Site | Google Scholar
D. J. Opperman and E. van Heerden, “Aerobic Cr(VI) reduction by Thermus scotoductus strain SA-01,” Journal of Applied Microbiology, vol. 103, no. 5, pp. 1907–1913, 2007.
View at: Publisher Site | Google Scholar
S. Farag and S. Zaki, “Identification of bacterial strains from tannery effluent and reduction of hexavalent chromium,” Journal of Environmental Biology, vol. 31, no. 5, pp. 877–882, 2010.
View at: Google Scholar
M. Z. Alam and S. Ahmad, “Toxic chromate reduction by resistant and sensitive bacteria isolated from tannery effluent contaminated soil,” Annals of Microbiology, vol. 62, no. 1, pp. 113–121, 2012.
View at: Publisher Site | Google Scholar
S. Dey and A. K. Paul, “Occurrence and evaluation of chromium reducing bacteria in seepage water from chromite mine quarries of Orissa, India,” Journal Water Research Protection, vol. 2, pp. 380–388, 2010.
View at: Google Scholar
S. Dey and A. K. Paul, “Optimization of cultural conditions for growth associated chromate reduction by Arthrobacter sp. SUK 1201 isolated from chromite mine overburden,” Journal of Hazardous Materials, vol. 213-214, pp. 200–206, 2012.
View at: Publisher Site | Google Scholar
S. Dey and A. K. Paul, “Hexavalent chromium reduction by aerobic heterotrophic bacteria indigenous to chromite mine overburden,” Brazilian Journal of Microbiology, vol. 44, no. 1, pp. 307–315, 2013.
View at: Publisher Site | Google Scholar
Y. Wang and C. Xiao, “Factors affecting hexavalent chromium reduction in pure cultures of bacteria,” Water Research, vol. 29, no. 11, pp. 2467–2474, 1995.
View at: Publisher Site | Google Scholar
J. J. Calomiris, J. L. Armstrong, and R. J. Seidler, “Association of metal tolerance with multiple antibiotic resistance of bacteria isolated from drinking water,” Applied and Environmental Microbiology, vol. 47, no. 6, pp. 1238–1242, 1984.
View at: Google Scholar
C. H. Park, M. Keyhan, B. Wielinga, S. Fendorf, and A. Matin, “Purification to homogeneity and characterization of a novel Pseudomonas putida chromate reductase,” Applied and Environmental Microbiology, vol. 66, no. 5, pp. 1788–1795, 2000.
View at: Publisher Site | Google Scholar
D. Bagchi, S. J. Stohs, B. W. Downs, M. Bagchi, and H. G. Preuss, “Cytotoxicity and oxidative mechanisms of different forms of chromium,” Toxicology, vol. 180, no. 1, pp. 5–22, 2002.
View at: Publisher Site | Google Scholar
E. Ezaka and C. U. Anyanwu, “Chromium (VI) tolerance of bacterial strains isolated from sewage oxidation ditch,” International Journal of Environmental Science, vol. 1, pp. 1725–1734, 2011.
View at: Google Scholar
W. C. Bae, H. K. Lee, Y. C. Choe et al., “Purification and characterization of NADPH-dependent Cr(VI) reductase from Escherichia coli ATCC 33456,” Journal of Microbiology, vol. 43, no. 1, pp. 21–27, 2005.
View at: Google Scholar
R. Elangovan, S. Abhipsa, B. Rohit, P. Ligy, and K. Chandraraj, “Reduction of Cr(VI) by a Bacillus sp.,” Biotechnology Letters, vol. 28, no. 4, pp. 247–252, 2006.
View at: Publisher Site | Google Scholar
P.-. Wang, T. Mori, K. Komori, M. Sasatsu, K. Toda, and H. Ohtake, “Isolation and characterization of an Enterobacter cloacae strain that reduces hexavalent chromium under anaerobic conditions,” Applied and Environmental Microbiology, vol. 55, no. 7, pp. 1665–1669, 1989.
View at: Google Scholar
P.-. Wang, K. Toda, H. Ohtake, I. Kusaka, and I. Yabe, “Membrane-bound respiratory system of Enterobacter cloacae strain HO1 grown anaerobically with chromate,” FEMS Microbiology Letters, vol. 78, no. 1, pp. 11–15, 1991.
View at: Publisher Site | Google Scholar
Z. He, F. Gao, T. Sha, Y. Hu, and C. He, “Isolation and characterization of a Cr(VI)-reduction Ochrobactrum sp. strain CSCr-3 from chromium landfill,” Journal of Hazardous Materials, vol. 163, no. 2-3, pp. 869–873, 2009.
View at: Publisher Site | Google Scholar
M. He, X. Li, H. Liu, S. J. Miller, G. Wang, and C. Rensing, “Characterization and genomic analysis of a highly chromate resistant and reducing bacterial strain Lysinibacillus fusiformis ZC1,” Journal of Hazardous Materials, vol. 185, no. 2-3, pp. 682–688, 2011.
View at: Publisher Site | Google Scholar
M. Megharaj, S. Avudainayagam, and R. Naidu, “Toxicity of hexavalent chromium and its reduction by bacteria isolated from soil contaminated with tannery waste,” Current Microbiology, vol. 47, no. 1, pp. 51–54, 2003.
View at: Publisher Site | Google Scholar
S. Dey and A. K. Paul, “Optimization of chromate reduction by whole cells of Arthrobacter sp. SUK 1205 isolated from metalliferous chromite mine environment,” Geomaterials, vol. 2, no. 4, pp. 73–81, 2012.
View at: Publisher Site | Google Scholar
A. Pal and A. K. Paul, “Aerobic chromate reduction by chromium-resistant bacteria isolated from serpentine soil,” Microbiological Research, vol. 159, no. 4, pp. 347–354, 2004.
View at: Publisher Site | Google Scholar
J. S. McLean, T. J. Beveridge, and D. Phipps, “Isolation and characterization of a chromium-reducing bacterium from a chromated copper arsenate-contaminated site,” Environmental Microbiology, vol. 2, no. 6, pp. 611–619, 2000.
View at: Publisher Site | Google Scholar
S. Sultan and S. Hasnain, “Reduction of toxic hexavalent chromium by Ochrobactrum intermedium strain SDCr-5 stimulated by heavy metals,” Bioresource Technology, vol. 98, no. 2, pp. 340–344, 2007.
View at: Publisher Site | Google Scholar
Y. G. Liu, W. H. Xu, and G. M. Zeng, “Experimental study on reduction by Pseudomonas aeruginosa,” Journal of Environmental Sciences, vol. 16, no. 5, pp. 797–801, 2004.
View at: Google Scholar
Y.-T. Wang and H. Shen, “Bacterial reduction of hexavalent chromium,” Journal of Industrial Microbiology, vol. 14, no. 2, pp. 159–163, 1995.
View at: Google Scholar
R. Batool, K. Yrjälä, and S. Hasnain, “Hexavalent chromium reduction by bacteria from tannery effluent,” Journal of Microbiology and Biotechnology, vol. 22, no. 4, pp. 547–554, 2012.
View at: Publisher Site | Google Scholar
M. A. Amoozegar, A. Ghasemi, M. R. Razavi, and S. Naddaf, “Evaluation of hexavalent chromium reduction by chromate-resistant moderately halophile, Nesterenkonia sp. strain MF2,” Process Biochemistry, vol. 42, no. 10, pp. 1475–1479, 2007.
View at: Publisher Site | Google Scholar
S. O. Farrell and R. T. Ranallo, Experiments in Biochemistry. A Hands-On Approach, Saunders College Publications, Orlando, Fla, USA, 2000.
J. Mclean and T. J. Beveridge, “Chromate reduction by a Pseudomonad isolated from a site contaminated with chromated copper arsenate,” Applied and Environmental Microbiology, vol. 67, no. 3, pp. 1076–1084, 2001.
View at: Publisher Site | Google Scholar
A. S. S. Ibrahim, M. A. El-Tayeb, Y. B. Elbadawi, and A. A. Al-Salamah, “Isolation and characterization of novel potent Cr(VI) reducing alkaliphilic Amphibacillus sp. KSUCR3 from hypersaline soda lakes,” Electronic Journal of Biotechnology, vol. 14, no. 4, p. 4, 2011.
View at: Publisher Site | Google Scholar
A. S. S. Ibrahim, M. A. El-Tayeb, Y. B. Elbadawi, and A. A. Al-Salamah, “Bioreduction of cr (VI) by potent novel chromate resistant alkaliphilic Bacillus sp. strain ksucr5 isolated from hypersaline soda lakes,” African Journal of Biotechnology, vol. 10, no. 37, pp. 7207–7218, 2011.
View at: Google Scholar
F. Abe, T. Miura, T. Nagahama, A. Inoue, R. Usami, and K. Horikoshi, “Isolation of a highly copper-tolerant yeast, Cryptococcus sp., from the Japan Trench and the induction of superoxide dismutase activity by Cu²⁺,” Biotechnology Letters, vol. 23, no. 24, pp. 2027–2034, 2001.
View at: Publisher Site | Google Scholar
R. Wani, K. M. Kodam, K. R. Gawai, and P. K. Dhakephalkar, “Chromate reduction by Burkholderia cepacia MCMB-821, isolated from the pristine habitat of alkaline crater lake,” Applied Microbiology and Biotechnology, vol. 75, no. 3, pp. 627–632, 2007.
View at: Publisher Site | Google Scholar
U. Thacker, R. Parikh, Y. Shouche, and D. Madamwar, “Hexavalent chromium reduction by Providencia sp.,” Process Biochemistry, vol. 41, no. 6, pp. 1332–1337, 2006.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2014 Satarupa Dey et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

1853

Downloads

517

Citations