Tests on Pretrained Superelastic NiTi Shape Memory Alloy Rods: Towards Application in Self-Centering Link Beams
Table 2
Accumulated residual strains at typical loading cycles.
| Specimens | Accumulated residual strains | After incremental cycles | After 5 constant cycles | After 10 constant cycles | After 15 constant cycles | After 20 constant cycles | After 25 constant cycles | ε0 (%) | ε0/ε25 (%) | ε5 (%) | ε5/ε25 (%) | ε10 (%) | ε10/ε25 (%) | ε15 (%) | ε15/ε25 (%) | ε20 (%) | ε20/ε25 (%) | ε25 (%) |
| D14/14-N-N | 3.56 | 89.67 | 3.87 | 97.48 | 3.93 | 98.99 | 3.95 | 99.50 | 3.96 | 99.75 | 3.97 | D14/14-300-30 | 1.38 | 60.00 | 1.91 | 83.04 | 2.10 | 91.30 | 2.20 | 95.65 | 2.27 | 98.70 | 2.30 | D14/14-350-30 | 0.49 | 40.50 | 0.76 | 62.81 | 0.93 | 76.86 | 1.06 | 87.60 | 1.16 | 95.87 | 1.21 | D14/14-400-30 | 0.53 | 38.13 | 0.84 | 60.43 | 1.03 | 74.10 | 1.16 | 83.45 | 1.31 | 94.24 | 1.39 | D14/14-450-30 | 1.61 | 53.67 | 2.49 | 83.00 | 2.73 | 91.00 | 2.86 | 95.33 | 2.93 | 97.67 | 3.00 |
|
|