Experimental Research on the Influence of Temperature on the Static Properties of Skarn
Table 2
Uniaxial compression test data (water cooling).
| Specimen number | Temperature (°C) | Diameter (mm) | Height (mm) | Quality (g) | Compressive strength (MPa) | Elastic modulus (GPa) | Peak strain (με) |
| YSL-1 | 25 | 50 | 100 | 653 | 250.19 | 82.01 | 3244 | YSL-2 | 25 | 50 | 100 | 662 | 260.17 | 83.65 | 3601 | YSL-3 | 25 | 50 | 100 | 656 | 242.70 | 79.40 | 3565 | YSL-4 | 200 | 50 | 100 | 649 | 236.35 | 51.45 | 4059 | YSL-5 | 200 | 50 | 100 | 653 | 232.02 | 56.84 | 4190 | YSL-6 | 200 | 50 | 100 | 660 | 237.42 | 44.28 | 3927 | YSL-7 | 400 | 50 | 100 | 670 | 136.21 | 23.16 | 5930 | YSL-8 | 400 | 50 | 100 | 662 | 125.64 | 20.04 | 6337 | YSL-9 | 400 | 50 | 100 | 659 | 147.78 | 26.73 | 5620 | YSL-10 | 600 | 50 | 100 | 655 | 110.31 | 9.76 | 9110 | YSL-11 | 600 | 50 | 100 | 668 | 108.22 | 10.11 | 9210 | YSL-12 | 600 | 50 | 100 | 663 | 115.31 | 9.94 | 9394 | YSL-13 | 800 | 50 | 100 | 660 | 32.28 | 1.59 | 13740 | YSL-14 | 800 | 50 | 100 | 672 | 38.70 | 1.37 | 14371 | YSL-15 | 800 | 50 | 100 | 668 | 33.91 | 1.83 | 13277 |
|
|
Note. YSL represents the specimen used for the uniaxial compression experiment after water cooling.
|