Experimental Research on the Influence of Temperature on the Static Properties of Skarn
Table 4
Brazilian disc splitting experiment test data (water cooling).
Specimen number
Temperature (°C)
Diameter (mm)
Thickness (mm)
Quality (g)
Failure load (kN)
Tensile strength (MPa)
Average value (MPa)
LSL-1
25
50
40.45
275
44.13
11.12
LSL-2
25
50
40.00
268
66.58
16.96
14.27
LSL-3
25
50
40.20
256
58.14
14.74
LSL-4
200
50
40.40
274
22.91
7.22
LSL-5
200
50
39.12
262
32.83
8.55
7.43
LSL-6
200
50
40.80
268
26.14
6.53
LSL-7
400
50
41.30
273
13.50
4.16
LSL-8
400
50
41.40
268
37.75
9.29
6.04
LSL-9
400
50
40.70
269
18.70
4.68
LSL-10
600
50
41.10
278
18.70
5.80
LSL-11
600
50
41.20
272
22.86
5.65
5.49
LSL-12
600
50
41.30
280
20.31
5.01
LSL-13
800
50
40.90
275
15.82
4.93
LSL-14
800
50
41.50
270
0
0
3.6
LSL-15
800
50
41.10
267
9.17
2.27
Notes. LSL represents the test piece used for Brazilian disc splitting experiment after water cooling. The data “0” indicates that the specimen has been damaged during heating or cooling.