Set no. | Set size | Material | Specimen size (mm) | Test speed | Standard | Reference |
tf | bf | lf |
|
1 | 7 | Glass/epoxy laminate | 1.5 | 12.7 | 25.4 | n.a. | n.a. | Rosen 1964 [14] |
2 | 5 | Glass/epoxy laminate | 1.5 | 12.7 | 25.4 | n.a. | n.a. | Zweben 1968 [15] |
3 | 6 | Glass/epoxy laminate | 1.5 | 12.7 | 25.4 | n.a. | n.a. |
4 | 13 | Carbon/epoxy laminate | n.a. | n.a. | n.a. | n.a. | n.a. | Bullock 1974 [16] |
5 | 36 | Carbon/epoxy tow | n.a. | n.a. | n.a. | n.a. | n.a. |
6 | 29 | Glass/epoxy prepreg | n.a. | 25.4 | 203 | n.a. | n.a. | Sun and Yamada 1978 [17] |
7 | 25 | Carbon/epoxy panel coupon | n.a. | 12.7 | 229 | n.a. | D3039 | Whitney and Knight 1980 [18] |
8 | 20 | Carbon/epoxy panel coupon | n.a. | 12.7 | 229 | n.a. | D3039 |
9 | 36 | Carbon/epoxy panel coupon | n.a. | 12.7 | 229 | n.a. | D3039 |
10 | 49 | S2-glass/epoxy | n.a. | n.a. | n.a. | n.a. | n.a. | Shimokawa et al. 1989 [19] |
11 | 30 | Carbon/epoxy laminate | n.a. | 38 | 300 | n.a. | n.a. | Beyerlein and Phoenix 1990 [20] |
12 | 31 | Carbon/epoxy microlaminate | n.a. | n.a. | n.a. | n.a. | n.a. | |
13 | 21 | Carbon/epoxy microlaminate | n.a. | n.a. | n.a. | n.a. | n.a. |
14 | 48 | Carbon/epoxy microlaminate | n.a. | n.a. | n.a. | n.a. | n.a. |
15 | 24 | Carbon/epoxy microlaminate | n.a. | n.a. | n.a. | n.a. | n.a. |
16 | 30 | Carbon/epoxy microlaminate | n.a. | n.a. | n.a. | n.a. | n.a. |
17 | 6 | Carbon/epoxy prepreg | 3.4 | 38.2 | 324 | 0.00047 s−1 | D3039 | Lavoie 1997 [21] |
18 | 7 | Carbon/epoxy prepreg | 4.5 | 50.9 | 431 | 0.00047 s−1 | D3039 | |
19 | 7 | Carbon/epoxy prepreg | 1.1 | 12.7 | 108 | 0.00047 s−1 | D3039 | |
20 | 7 | Carbon/epoxy prepreg | 2.2 | 25.5 | 219 | 0.00047 s−1 | D3039 | |
21 | 7 | Carbon/epoxy prepreg | 3.4 | 38.2 | 324 | 0.00047 s−1 | D3039 | |
22 | 7 | Carbon/epoxy prepreg | 1.1 | 12.7 | 108 | 0.00047 s−1 | D3039 | |
23 | 8 | E-glass/epoxy laminate | 1.6 | 100 | 250 | 3 mm/min | n.a. | Cattell and Kibble 2001 [22] |
24 | 14 | E-glass/epoxy laminate | 1.0 | 100 | 250 | 3 mm/min | n.a. | |
25 | 20 | Carbon/epoxy laminate | 8.0 | 10 | 60 | 2.64 mm/min | D3039 | Ochola 2004 [23] |
26 | 20 | Glass/epoxy laminate | 8.0 | 10 | 60 | 2.64 mm/min | D3039 | |
27 | 19 | Carbon/epoxy sheet | 0.89 | 15 | 206 | 1.33 mm/min | D3039 | Birgoren and Husnu Dirikolu 2004 [24] |
28 | 6 | E-glass/epoxy | 1.2 | 15 | 250 | 1 mm/min | ISO 527 | Makarov et al. 2004 [25] |
29 | 5 | E-glass/epoxy | 1.2 | 15 | 250 | 3.8 s−1 | n.a. | |
30 | 5 | E-glass/epoxy | 1.2 | 15 | 250 | 22.65 s−1 | n.a. | Makarov et al. 2004 [25] |
31 | 5 | E-glass/epoxy | 1.2 | 15 | 250 | 32.34 s−1 | n.a. | |
32 | 5 | E-glass/epoxy | 1.2 | 15 | 250 | 39.85 s−1 | n.a. | |
33 | 5 | E-glass/epoxy | 1.2 | 15 | 250 | 40.89 s−1 | n.a. | |
34 | 30 | E-glass/vinyl ester coupon | 6.4 | 25.4 | 330 | 2.5 mm/min | D3039 | Zureick et al. 2006 [3] |
35 | 30 | E-glass/vinyl ester coupon | 9.6 | 25.4 | 330 | 2.5 mm/min | D3039 | |
36 | 24 | E-glass/vinyl ester coupon | 6.4 | 25.4 | 330 | 2.5 mm/min | D3039 | |
37 | 24 | E-glass/vinyl ester coupon | 6.4 | 25.4 | 330 | 2.5 mm/min | D3039 | |
38 | 30 | E-glass/vinyl ester coupon | n.a. | n.a. | n.a. | n.a. | n.a. | |
39 | 5 | Glass/epoxy laminate | 1.0 | 12.7 | 82.7 | 0.0017 s−1 | n.a. | Shokrieh and Omidi 2009 [26] |
40 | 5 | Glass/epoxy laminate | 1.0 | 12.7 | 82.7 | 0.55 s−1 | n.a. | |
41 | 5 | Glass/epoxy laminate | 1.0 | 12.7 | 82.7 | 5.6 s−1 | n.a. | |
42 | 5 | Glass/epoxy laminate | 1.0 | 12.7 | 83.7 | 46 s−1 | n.a. | |
43 | 5 | Glass/epoxy laminate | 1.0 | 12.7 | 82.7 | 85 s−1 | n.a. | |
44 | 30 | Carbon/epoxy plate | 1.0 | 5.0 | 120 | 0.5 mm/min | n.a. | Okabe et al. 2010 [27] |
45 | 20 | Carbon/epoxy laminate | 2.0 | 25 | 230 | 2 mm/min | GB/T3354 | Wang and yang 2010 [28] |
46 | 20 | Carbon/epoxy laminate | 2.0 | 15 | 175 | 2 mm/min | D3039 | Du et al. 2012 [29] |
47 | 7 | Glass/polyester panel coupon | 1.0 | 15 | 250 | 2 mm/min | D3039 | Gohil and Shaikh 2013 [8] |
48 | 60 | Carbon/epoxy panel coupon | 0.8 | 12.5 | 330 | 2 mm/min | D3039 | Sasikumar et al. 2015 [30] |
49 | 9 | Glass/epoxy laminate | 0.6 | 2.64 | 105 | 120 s−1 | n.a. | Ou and Zhu 2015 [13] |
50 | 8 | Glass/epoxy laminate | 0.6 | 2.64 | 105 | 40 s−1 | n.a. | |
51 | 10 | Glass/epoxy laminate | 0.52 | 22 | 105 | 1/600 s−1 | n.a. | Ou et al. 2016 [31] |
52 | 9 | Glass/epoxy laminate | 0.52 | 22 | 105 | 50 s−1 | n.a. | |
53 | 8 | Glass/epoxy laminate | 0.52 | 22 | 105 | 40 s−1 | n.a. | |
54 | 8 | Glass/epoxy laminate | 0.52 | 22 | 105 | 40 s−1 | n.a. | |
55 | 72 | Carbon/polyamide6 laminate | 1.0 | 25 | 250 | 1 mm/min | JISK7165 | Ma et al. 2016 [32] |
56 | 58 | Carbon/epoxy laminate | 1.0 | 25 | 250 | 1 mm/min | JISK7165 | |
57 | 59 | Carbon/polyamide6 laminate | 1.0 | 15 | 250 | 1 mm/min | D3039 | Ma et al. 2017 [33] |
58 | 67 | Carbon/epoxy laminate | 1.0 | 15 | 250 | 1 mm/min | D3039 | |
|