Experimental Study on the Effect of Large Temperature Difference on Compressive Strength and Pore Structure of Semirigid Base
Table 8
Experimental results of dynamic modulus of semirigid base material under the temperature range of −20°C∼20°C.
| Number of cycles | Parallel modulus test value (MPa) | Modulus representative value (MPa) | Standard deviation | Coefficient of variation (%) |
| 0 | 17129 | 16249 | 18480 | 17286 | 1123.68 | 6.50 | 3 | 5483 | 6142 | 7250 | 6292 | 892.98 | 14.19 | 6 | 4453 | 4622 | 5678 | 4918 | 663.91 | 13.50 | 9 | 4034 | 4790 | 5029 | 4618 | 519.85 | 11.26 | 12 | 4834 | 3928 | 4333 | 4365 | 453.82 | 10.40 | 15 | 3783 | 3566 | 4717 | 4022 | 611.69 | 15.21 |
|
|