Heterostructures for Realizing Magnon-Induced Spin Transfer Torque

<table>XRD Phi scans of Fe<sub>3</sub>O<sub>4</sub> on MgO (100) substrates. (a) Complete scan on (220) plane, (b) complete scan on (311) plane, (c) MgO (220) peak, FWHM = 0.38°, (d) Fe<sub>3</sub>O<sub>4</sub> (220) Peak, FWHM = 1.36° (e) MgO (311) peak, FWHM = 0.56° (f) Fe<sub>3</sub>O<sub>4</sub> (311) peak, FWHM = 1.34°.</table>

Advances in Condensed Matter Physics

fig2

Figure 2

Figure 2: Heterostructures for Realizing Magnon-Induced Spin Transfer Torque 