Stress-Driven Evolution on Mismatched Ca2Co2O5 Oxide Material: From Geometry to the Electronic States
Table 2
Binding lengths and binding numbers within sandwiched Ca2Co2O5 crystalline oxide.
| | 0 GPa | 1 GPa |
| CoO2 layer | Co-O | Length (Å) | Number | Length (Å) | Number | 1.802 | 0.53 | 1.805 | 0.52 | 1.773 | 0.56 | 1.772 | 0.56 |
| CaCoO layer | Co-O | 1.879 | 0.48 | 1.871 | 0.48 | 1.890 | 0.47 | 1.887 | 0.47 | 1.990 | 0.36 | 1.994 | 0.36 | 2.328 | 0.40 | 2.321 | 0.41 | Ca-O | 2.391 | 0.10 | 2.392 | 0.10 | 2.356 | 0.25 | 2.349 | 0.25 | 2.384 | 0.19 | 2.410 | 0.19 |
| Angle (°) | O-Co-O | 159.610 | — | 161.355 | — |
|
|