Morphological Investigation of Foamed Aluminum Parts Produced by Melt Gas Injection
Table 2
Mould filling ability.
| Mould type | Pressure | Gas | Dimension
(mm) | Sample
height (mm) | Filling |
| SM | Ambient | Nitrogen | ∅ 64 | 73.01 | 73.0% | SM | Ambient | Air | ∅ 64 | 86.76 | 86.8% | SM | Suction | Nitrogen | ∅ 64 | 62.95 | 62.9% |
ME | Ambient |
Nitrogen | L 19 | 66.50 | 83.1% | L 32 | 61.31 | 76.6% | ME | Ambient | Air | L 32 | 55.21 | 69.0% | ME |
Suction | Nitrogen | L 19 | 72.65 | 90.8% | L 32 | 72.79 | 91.0% |
BM | Suction |
Nitrogen | ∅ 24 | 161.0 | 73.2% | ∅ 28 | 122.8 | 55.8% | ∅ 32 | 199.5 | 90.7% |
BM | Suction |
Air | ∅ 24 | 111.0 | 50.4% | ∅ 28 | 77.55 | 35.2% | ∅ 32 | 212.0 | 96.4% |
|
|