Crystallization Behavior and Microstructural Analysis of Strontium Rich (Pb_𝑥Sr_𝟏−𝑥)TiO_𝟑 Glass Ceramics in Presence of La_𝟐O_𝟑

Table 3

Density of glass and glass ceramic, crystal structure, lattice parameters, and axial ratio of major crystalline phase in different strontium-rich glass ceramic samples in the system [(Pb_xSr_1-x ) O·TiO₂]- [2SiO₂·B₂O₃]-[K₂O]-[BaO]-1La₂O₃.

Glass code	Density (gm/cc)	Glass ceramic	Density (gm/cc)	Crystal structure	Lattice parameters, a (Å)	(PbSr)TiO3 ceramic*, a (Å)
4PL5B	3.827	4PL5B820T	3.856	Cubic	3.915±0.006	3.927
		4PL5B820S	4.109	Cubic	3.913±0.002
3PL5B	3.635	3PL5B871T	4.208	Cubic	3.911±0.000	3.943
		3PL5B871S	3.256	Cubic	3.902±0.003
2PL5B	3.507	2PL5B870T	3.961	Cubic	3.899±0.001	3.880
		2PL5B870S	3.671	Cubic	3.904±0.005
1PL5B	3.384	1PL5B878T	3.857	Cubic	3.904±0.001	3.880
		1PL5B878S	3.426	Cubic	3.895±0.002
STL5B	3.212	STL5B890T	3.261	Cubic	3.897±0.000	3.904
		STL5B890S	3.386	Cubic	3.901±0.000

*Reference [19].
The glass codes, density of glass and glass ceramics, crystal structure and lattice parameters are shown in Table 3.