Effect of Induced Charge on the Passivity and Passivity Breakdown of 304LN Stainless Steels
Table 3
Corrosion data with and without induced charge below pitting potential.
| Sample | () | (mA/cm2) |
| Without charge in 0.15N KCl solution | −0.25 | 0.19 | With positive charge in 0.15N KCl solution | −0.2 | 0.19 | With negative charge in 0.15N KCl solution | −0.2 | 0.24 | Without charge in 0.2N KCl solution | −0.41 | 0.27 | With positive charge in 0.2N KCl solution | −0.4 | 0.23 | With negative charge in 0.2N KCl solution | −0.4 | 0.3 | Without charge in 0.25N KCl solution | −0.38 | 0.28 | With positive charge in 0.25N KCl solution | −0.35 | 0.26 | With negative charge in 0.25N KCl solution | −0.3 | 0.29 |
|
|