Thermal Effect on Structure of Silver in Ion-Exchanged Soda-Lime Glasses and Aluminum-Doped Zinc Oxide Films

Table 2

The d-spacing between (002) planes in AZO films under different conditions.

Film condition	2θ (°)	d-spacing (Å)
As-deposited at room temperature	34.18	2.621
After 100°C annealing and cooling down to room temperature	34.14	2.624
After 200°C annealing and cooling down to room temperature	34.16	2.623
After 300°C annealing and cooling down to room temperature	34.16	2.623
After 400°C annealing and cooling down to room temperature	34.42	2.603