Advances in Materials Science and Engineering / 2013 / Article / Tab 4 / Research Article
Experimental Study of Correlation of Mechanical Properties of Al-Si Casts Produced by Pressure Die Casting with Si/Fe/Mn Content and Their Mutual Mass Relations Table 4 Values of chemical compositions of particular cast samples and values of residual deformation.
Sample Si (%) Fe (%) Cu (%) Mn (%) Mg (%) Zn (%) Ni (%) Cr (%) Pb (%) Sn (%) Ti (%) V (%) Al (%) Def. (mm) A1 9.87 0.91 2.27 0.28 0.14 0.74 0.06 0.03 0.12 0.04 0.03 0.01 85.50 0.293 B1 9.88 0.89 2.31 0.27 0.13 0.76 0.06 0.03 0.12 0.04 0.03 0.01 85.48 0.290 A2 9.72 0.87 2.24 0.26 0.14 0.74 0.06 0.03 0.12 0.04 0.03 0.01 85.74 0.296 B2 9.76 0.88 2.22 0.27 0.13 0.74 0.06 0.03 0.12 0.04 0.03 0.01 85.71 0.292 A3 9.72 0.87 2.29 0.26 0.13 0.76 0.06 0.03 0.12 0.04 0.03 0.01 85.68 0.295 B3 9.51 0.86 2.2 0.27 0.12 0.74 0.06 0.03 0.11 0.04 0.03 0.01 85.99 0.291 A4 9.49 0.87 2.24 0.27 0.13 0.75 0.06 0.03 0.12 0.05 0.03 0.01 85.95 0.316 B4 9.39 0.85 2.21 0.25 0.13 0.73 0.06 0.03 0.12 0.04 0.03 0.01 86.14 0.313 A5 9.41 0.83 2.24 0.25 0.13 0.74 0.06 0.03 0.12 0.05 0.03 0.01 86.08 0.312 B5 9.48 0.85 2.24 0.25 0.13 0.74 0.06 0.03 0.12 0.05 0.03 0.01 86.00 0.311 A6 9.3 0.82 2.19 0.25 0.14 0.76 0.06 0.03 0.12 0.05 0.03 0.01 86.20 0.327 B6 9.47 0.85 2.21 0.25 0.14 0.76 0.06 0.03 0.12 0.05 0.03 0.01 86.02 0.305 A7 9.49 0.85 2.22 0.24 0.13 0.75 0.06 0.03 0.12 0.04 0.03 0.01 86.03 0.316 B7 9.41 0.83 2.16 0.25 0.13 0.75 0.06 0.03 0.11 0.04 0.03 0.01 86.19 0.306 A8 9.32 0.81 2.25 0.22 0.13 0.75 0.06 0.02 0.12 0.05 0.03 0.01 86.23 0.334 B8 9.28 0.83 2.24 0.23 0.13 0.75 0.06 0.02 0.12 0.05 0.03 0.01 86.25 0.338 A9 9.34 0.81 2.28 0.22 0.13 0.75 0.06 0.02 0.12 0.05 0.02 0.01 86.19 0.331 B9 9.23 0.79 2.21 0.23 0.13 0.76 0.06 0.02 0.12 0.05 0.03 0.01 86.36 0.336 A10 9.44 0.81 2.25 0.23 0.13 0.75 0.06 0.03 0.12 0.05 0.03 0.01 86.09 0.33 B10 9.32 0.8 2.24 0.22 0.13 0.73 0.06 0.03 0.12 0.04 0.04 0.01 86.26 0.323