Defect Study of MgO-CaO Material Doped with CeO2
Table 1
Calculated lattice constant for sintered samples.
| Sample | Parameters | (h k l) | (Å) | (1 1 1) | (2 0 0) | (2 2 0) | (3 1 1) | (2 2 2) |
| 0% CeO2 | 2 (°) | 32.33 | 37.51 | 54.09 | 64.35 | 67.70 | 4.7978 | (Å) | 2.7681 | 2.3981 | 1.6960 | 1.4471 | 1.3853 | 0.5 wt% CeO2 | 2 (°) | 32.34 | 37.50 | 54.04 | 64.36 | 67.54 | 4.8232 | (Å) | 2.7661 | 2.3966 | 1.6961 | 1.4468 | 1.3854 | 0.75 wt% CeO2 | 2 (°) | 32.37 | 37.52 | 54.07 | 64.36 | 67.60 | 4.8223 | (Å) | 2.7630 | 2.3942 | 1.6953 | 1.4463 | 1.3850 | 1 wt% CeO2 | 2 (°) | 32.34 | 37.52 | 54.05 | 64.34 | 67.62 | 4.8161 | (Å) | 2.7655 | 2.3961 | 1.6960 | 1.4468 | 1.3852 |
|
|