Abstract

Calcium hydroxyapatite, CaHAp, synthesized by the precipitation method, was utilized to study the calcium-lead metathesis reaction on dissolution in a lead nitrate solution under reflux conditions to prepare larger lead hydroxyapatite, PbHAp, crystals from CaHAp. SEM images show development of crystalline PbHAp on the surfaces of CaHAp. The needle-like crystal morphology observed for PbHAp after 24 h reaction time developed into hexagonal-rod crystal morphology within 48 h reaction time. The largest PbHAp crystals obtained from 48 h reaction time have approximate size of 10 × 10 × 40 μm. Powder X-ray diffraction results show mixed phases of CaHAp and PbHAp due to difficulty in separating the PbHAp product from the CaHAp substrate. The PbHAp peaks observed after 24 h of reaction sharpen and increase in intensity after 48 h of reaction confirming that the PbHAp phase is the major product for the 48 h reaction time. EDX results of the crystalline products show high intensity Pb peaks with lead to phosphorous ratio (5 : 3) as expected for PbHAp. Lower intensity Ca peaks are also observed, consistent with incomplete coverage of the CaHAp growth substrate.

1. Introduction

Calcium hydroxyapatite, Ca5(PO4)3(OH), CaHAp, the prototype structure of the apatite series, is the dominant component in biological hard tissues such as bones (about 69 wt% CaHAp) and teeth (about 95 wt% CaHAp) [1]. The structure belongs to space group and is susceptible to ionic substitution in both anion and cation sites. Ca2+ can be replaced by various divalent cations including Fe2+, Cr2+, Zn2+, Mg2+, Cd2+, Sr2+, or Pb2+ [26], can be replaced by or , and OH can be replaced by F or Cl [710].

Complete substitution of Pb2+ ions into CaHAp structure results in the isostructural lead hydroxyapatite, sometimes called hydroxypyromorphite, Pb5(PO4)3(OH), PbHAp, which has been studied, including its structure [11, 12] and solubility properties [13], partly because the accumulation of Pb2+ in bones accompanies bone diseases. Chronic exposure to lead has been shown to inhibit skeletal development [14] and/or can lead to osteoporosis [15] as the lead localizes in the area of bone formation and resorption, respectively. It is possible that this is a consequence of the lower solubility of PbHAp [16] compared to CaHAp [17]. Thus, the relationship between CaHAp and PbHAp in terms of their structure and properties as well as their potential interconversions might provide important keys in the understanding of the accumulation of Pb2+ in bone.

Studies on the mechanism and phase evolution of Pb2+ immobilization by synthetic CaHAp have been reported [18, 19] and show dissolution of CaHAp in Pb2+ solution and then concomitant crystallization of PbHAp in the system. The mechanism of PbHAp formation in acidic conditions has been proposed [20, 21] as follows.Dissolution of CaHAp: Precipitation of PbHAp: Earlier studies of Pb2+ immobilization by hydroxyapatite in the absence of potential substitution ions [22], in the presence of potential substitution anions [23], and in the presence of potential substitution cations [24] show the same dissolution/precipitation mechanism. While the Ca2+ and Pb2+ compounds are isostructural, they are in separate series due to the difficulty of substituting Pb for Ca in the apatite series or of substituting Ca for Pb in the pyromorphite series [25].

This work reports preparation of CaHAp and its X-ray absorption spectroscopy (XAS) spectrum to characterize the short-range environment around Ca absorbing atoms of the precipitate product. A reflux method was used to increase the CaHAp dissolution rate and thus the PbHAp crystallization rate in the metathesis reaction of CaHAp in lead nitrate solution. The relationship between reaction times and crystal morphologies of products is discussed.

2. Materials and Methods

2.1. Preparation of CaHAp Material

Phosphate and calcium solutions for preparation of CaHAp were prepared by dissolving 7.92 g (60 mmol) diammonium hydrogen phosphate, (NH4)2HPO4 (Ajax Finechem, AR grade), in 100 mL deionized water and dissolving 23.60 g (100 mmol) calcium nitrate, Ca(NO3)2·4H2O (Ajax Finechem, AR grade), in 100 mL deionized water. CaHAp was prepared by dropwise addition of phosphate solution into calcium solution, while stirring at room temperature and maintaining the solution pH at 11 with 1.0 M NaOH. After addition of the phosphate solution, the suspension was stirred continuously for 30 min and the precipitate was separated by filtration, washed with deionized water three times, and dried at 100°C for 24 h.

2.2. Preparation of PbHAp by Reflux Method

Excess CaHAp, 0.20 g (3.98 mmol), was ground in an agate mortar and added into a solution prepared by dissolving 0.0733 g (0.22 mmol) lead nitrate, Pb(NO3)2 (Ajax Finechem, AR grade), in 80 mL deionized water and refluxed for 24 h and 48 h. The white precipitates were separated by filtration, washed with deionized water three times, and dried at 100°C for 24 h.

2.3. Characterization

Crystal morphologies were observed by scanning electron microscopy (SEM) using a JSM 6400 electron microscope (JEOL, Japan) equipped with a Microspec model WDX-100 energy dispersive X-ray fluorescence (EDX) detector. IR spectra were acquired on a Perkin-Elmer model Spectrum GX Fourier transform infrared spectrophotometer in wavenumber range 400–4000 cm−1 from KBr pellets.

Powder X-ray diffraction (XRD) scans were acquired for the 2θ range 10–55° on a Bruker Analytical X-ray Systems D5005 diffractometer equipped with a Cu Kα sealed tube X-radiation source operating at 40 kV and 40 mA. Comparison with ICDD JCPDS files [26] was utilized for phase identification of products.

X-ray absorption spectroscopy (XAS) experiments were conducted at the BL-8 beamline at the Siam Photon Laboratory of the National Synchrotron Research Center of Thailand (Nakhon Ratchasima, Thailand) with the electron storage ring operated at 1.2 GeV with an average beam current of ~100 mA. A monochromatic beam was obtained by means of a Si(111) double crystal monochromator. Experiments were performed at the Ca K-edge in transmission mode. The gas ionization chamber was filled with N2 (~400 mbar), and XAS spectra of CaCl2·2H2O were used for a standard energy calibration (4042 eV). Extended X-ray absorption fine structure, EXAFS, spectra were collected in an energy range between 3970 and 4750 eV, with energy steps of 1 eV. Samples and reference compounds were ground in an agate mortar in air until uniform and were sealed between layers of Kapton tape on the sample holder and then brought to the beam. EXAFS fitting was carried out using the IFEFFIT library [27] within the ATHENA XAS data processing suite [28], and interatomic distance estimates were obtained from the ATHENA suite [29].

3. Results and Discussion

CaHAp structure has been reported [30, 31]. It consists of metal atoms located on two crystallographically different sites: sites (identified as Ca(I)) and sites (identified as Ca(II)) as shown in Figure 1. Two metal ions at the Ca(I) sites are coordinated with nine O atoms (six shorter bonds to three O(1) and three O(2) phosphate oxygen atoms on Ca(I) sites define a twisted trigonal prism, and three longer bonds to O(3) atoms extend through the prism faces), and three metal ions at the Ca(II) sites are coordinated with seven O atoms (one O(1), one O(2), and four general O(3) atoms from groups and one O(4) atom from an OH group).

EXAFS fitting for CaHAp used the crystallographic parameters for ideally crystalline CaHAp taken from Posner et al. [30]. EXAFS data were Fourier-transformed in the range 2–10.5 Å−1 using -weighting of data and fit in real space in the range of 1–6 Å of the Ca local environment. Figure 2 shows EXAFS of (a) the -weighted raw and fitted (chi) functions of the samples and (b) Fourier transformations of -weighted EXAFS spectra. This is the best fit for these available EXAFS spectra. The distances displayed on the -axis are not corrected for phase shifts and appear offset by about 0.3 Å. The coordination number that is detected by EXAFS spectroscopy is composed of the weighted sum of Ca(I) and Ca(II) sites. Higher shells of light backscattering atoms were omitted due to small intensity, and shells in very close neighborhood were combined in order to keep the number of fit parameters manageable and mathematically significant. Multiple scattering pathways were of negligible magnitude. These results show an average bond distance of all atoms surrounding Ca atoms, Ca–O#1 = 2.41 Å (for Ca–6O), Ca–P#2 = 3.22 Å (Ca–2.4P), Ca–P#3 = 3.59 Å (Ca–2.4P), Ca(I)–Ca(II)#4 = 3.95 Å (Ca–6Ca), Ca(I)–Ca(II)#5 = 4.03 Å (Ca–2.4Ca), and Ca(I)–Ca(I)#6 = 5.45 Å (Ca–3.6Ca).

The SEM images of CaHAp before and after refluxing in lead nitrate solution are shown in Figure 3. Crystalline product after refluxing for 24 h exhibits needle-like crystal morphology on the surface of the CaHAp substrate (Figure 3(b)) while the crystalline product after refluxing for 48 h exhibits hexagonal-rod crystal morphology (Figure 3(c)). The product crystal size increased with increasing reaction time; the largest crystal size observed is about 10 × 10 × 40 μm. The finely divided PbHAp phase could not be easily separated from the CaHAp substrate.

EDX spectra of products and the substrate after refluxing in lead nitrate solution are shown in Figure 4. The EDX spectrum of the post reaction CaHAp substrate (Figure 4(a)) shows high intensity Ca peaks with calcium to phosphorous ratio of about 5 : 3 as expected for CaHAp (but no evidence of Pb peaks), while the spectrum of crystalline product region (Figure 4(b)) shows high intensity Pb peaks with lead to phosphorous ratio of 5 : 3 as expected for PbHAp. Low intensity Ca peaks are also observed in the product spectra, consistent with incomplete coverage of the CaHAp growth substrate. Similar spectra (not shown) were observed for the CaHAp substrate and PbHAp product areas after refluxing for 48 h. These spectra support the dissolution/precipitation mechanism previously proposed [20, 21] and do not give any suggestion of substitution of Ca2+ by Pb2+ in the CaHAp substrate to form a solid solution under the mild conditions of refluxing in H2O.

XRD patterns of products after refluxing for 24 h and 48 h also show mixed PbHAp (JCPDS number 08-0259) and CaHAp (JCPDS number 09-0432) phases as shown in Figure 5.

The XRD pattern of the product after 48 h reflux clearly shows the PbHAp phase as the major product phase with the intensity of PbHAp peaks considerably increased, indicating that formation of PbHAp phase increased with increased reaction time which is in agreement with previous work [18]. PbHAp crystal product is present as hexagonal rod-shaped crystals as shown in Figure 3(c). The presence of both phases results from difficulty separating the finely divided PbHAp phase from the approximately 20-fold excess CaHAp reactant substrate phase.

IR spectra of CaHAp and products after refluxing in the presence of Pb+2 (Figure 6) show bands in the appropriate regions: and stretching modes in the 961–1095 cm−1 region, bending mode in the 467–473 cm−1 region, and the bending mode in the 562–632 cm−1 region, consistent with previous reports for CaHAp [32, 33] and PbHAp [34].

The CaHAp reactant material was not calcined and shows broad water O–H stretching vibrational bands centered about 3468 cm−1 in the CaHAp spectrum with the apatite band as a shoulder at 3568 cm−1, similar to reported values of 3573 [32] and 3569 cm−1 [33]. A small sharp O–H stretching mode appears at 3571 cm−1 in the product spectra, which compares favorably with the apatite bands and the reported [34] vibrational stretching band for pure PbHAp at 3560 cm−1. A broad band in the 3000–3700 cm−1 region and a weak peak at 1639 cm−1 in the CaHAp spectrum are consistent with absorbed H2O on the KBr pellet or associated with the reactant substrate phase. As all the IR spectroscopy samples were prepared in the same manner, loss of these broad peaks on refluxing indicates that they are due to water associated with the reactant substrate phase.

The IR spectrum of CaHAp also shows bands of stretching at 1384 cm−1 and bending at 873 cm−1 in agreement with previous work [35]. The carbonate may come from the incorporation of atmospheric CO2 through equilibrium with the alkaline reaction solution during the synthesis step. The incorporation of into CaHAp materials has been suggested to increase the solubility of CaHAp [36].

4. Conclusion

The reflux method of CaHAp dissolution to provide phosphate anion in the presence of lead cation succeeds for producing larger sized crystals of the less soluble PbHAp from the aqueous solution. Hexagonal rod-shaped crystals of PbHAp formed and product crystal size increased with increasing reflux-reaction time. EDX results are consistent with the XRD results and show mixed phases of PbHAp and substrate CaHAp, but no evidence of Pb substitution into the CaHAp substrate phase. IR results indicate the incorporation of carbonate in the CaHAp substrate resulting in increased solubility of this material, but the carbonate anion does not appear to carry over into the PbHAp product crystals.

Conflict of Interests

The authors declare that there is no conflict of interests regarding the publication of this paper.