Estimation of the Pumping Pressure from Concrete Composition Based on the Identified Tribological Parameters
Table 4
Concretes compositions used in the study of Kaplan [
4].
| Concretes | W/C | (m3) | A/S | Sp/Sp* |
(mm) | Rheological parameters | Tribological parameters | Pumping pressures | Slump (cm) | (Pa) |
(Pa) | (Pa·s/m) |
(Pa) | (Pa·s/m) |
(Pa) | (Pa·s/m) |
(bar) | (bar) | (bar) |
| C=/52/FL | 0.48 | 0.318 | 1.06 | 0 | 2.24 | 16 | 1221 | 808 | 73 | 111 | 470 | 60.9 | 487.7 | 25.0 | 25.2 | 22.9 | C=/38/FL | 0.53 | 0.338 | 0.58 | 0 | 2.57 | 16 | 1221 | 722 | 31 | 85 | 344 | 60.9 | 315.9 | 18.5 | 17.3 | 16.0 | C=/66/FL | 0.51 | 0.333 | 1.80 | 0 | 1.94 | 18 | 1077 | 1017 | 71 | 79 | 357 | 54.4 | 399.8 | 18.7 | 16.3 | 19.0 | C−/52/FL | 0.57 | 0.311 | 1.17 | 0 | 1.87 | 18 | 1077 | 473 | 73 | 64 | 267 | 54.4 | 281.0 | 14.2 | 16.7 | 14.3 | C−/38/FL | 0.61 | 0.328 | 0.60 | 0 | 2.37 | 18 | 1077 | 440 | 50 | 56 | 252 | 54.4 | 196.0 | 13.2 | 16.0 | 10.9 | C−/66/FL | 0.61 | 0.324 | 1.82 | 0 | 1.69 | 20 | 932 | 743 | 59 | 53 | 244 | 48.0 | 230.8 | 12.7 | 14.1 | 11.9 | C=/52/TP | 0.57 | 0.292 | 1.08 | 0 | 2.22 | 14 | 1365 | 0 | 0 | 81 | 288 | 67.4 | 347.0 | 0.0 | 0.0 | 0.0 | C=/38/TP | 0.64 | 0.315 | 0.57 | 0 | 2.24 | 13 | 1437 | 775 | 51 | 75 | 290 | 70.7 | 238.6 | 15.8 | 14.2 | 13.5 | C+/52/TP | 0.50 | 0.313 | 1.04 | 0 | 2.18 | 12 | 1509 | 1314 | 94 | 150 | 455 | 73.9 | 551.9 | 26.6 | 30.1 | 26.2 | C+/38/TP | 0.52 | 0.318 | 0.60 | 0 | 2.62 | 15 | 1293 | 554 | 50 | 81 | 338 | 64.2 | 343.8 | 18.0 | 22.7 | 17.3 | C+/66/TP | 0.49 | 0.308 | 1.96 | 0 | 1.63 | 13 | 1437 | 976 | 90 | 89 | 349 | 70.7 | 651.9 | 18.9 | 21.1 | 22.9 | C−/52/TP | 0.69 | 0.279 | 1.07 | 0 | 1.98 | 15 | 1293 | 696 | 82 | 58 | 207 | 64.2 | 204.7 | 11.5 | 12.4 | 11.8 | C−/38/TP | 0.76 | 0.304 | 0.60 | 0 | 2.22 | 13 | 1437 | 556 | 78 | 170 | 206 | 70.7 | 161.6 | 17.8 | 10.0 | 10.4 | C+/52/FL | 0.34 | 0.297 | 1.08 | 0.8 | 1.94 | 21 | 860 | 378 | 351 | 260 | 587 | 33.5 | 939.5 | 37.8 | 35.7 | 38.9 | C+/38/FL | 0.40 | 0.323 | 0.57 | 0.8 | 2.45 | 21 | 860 | 403 | 132 | 50 | 470 | 33.5 | 474.0 | 21.5 | 25.0 | 20.8 | C+/66/FL | 0.38 | 0.317 | 1.88 | 0.8 | 1.52 | 22 | 788 | 377 | 121 | 104 | 664 | 30.3 | 870.9 | 32.0 | 28.9 | 35.6 | _0,5% | 0.41 | 0.330 | 1.01 | 0.2 | 2.12 | 16 | 1221 | 1173 | 88 | 100 | 622 | 58.1 | 719.8 | 25.6 | 28.8 | 26.9 | _1% | 0.36 | 0.305 | 1.09 | 0.4 | 1.90 | 19 | 1005 | 1200 | 50 | 0 | 718 | 45.6 | 920.1 | 24.1 | 25.7 | 27.0 | _1,5% | 0.37 | 0.311 | 1.08 | 0.6 | 1.88 | 21 | 860 | 655 | 175 | 50 | 778 | 36.3 | 748.7 | 28.4 | 21.4 | 26.8 | _2% | 0.35 | 0.301 | 1.07 | 0.8 | 1.87 | 20 | 932 | 900 | 270 | 32 | 926 | 36.8 | 883.2 | 32.5 | 40.1 | 31.3 |
|
|