Effects of Rolling Reduction and Strength of Composed Layers on Bond Strength of Pure Copper and Aluminium Alloy Clad Sheets Fabricated by Cold Roll Bonding

Figure 9

(a) Area fraction of deposit and (b) apparent tensile shear strengths obtained from tensile shear tests, corrected tensile shear strength with considering the area fraction of deposit on the fracture interface, and tensile shear strengths converted from the ultimate tensile strength of the Al alloy layers for Cu/Al-50%, Cu/Al-75%, Cu/AA5052-50%, Cu/AA5052-75%, Cu/AA5083-50%, and Cu/AA5083-75%.