Effect of Liquid Phase Additions on Microstructure and Thermal Properties in Copper and Copper-Diamond Composites

Figure 3

Graph of piston displacement of two different FAST experiments at temperatures 760°C and 825°C. Both runs were conducted at 50°C min⁻¹ with a load of 45 MPa. It is evident from the plot that the material quickly changes from solid to liquid at 780°C.