Nanocrystalline 6061 Al Powder Fabricated by Cryogenic Milling and Consolidated via High Frequency Induction Heat Sintering

<table>True stress strain response in simple compression for consolidated samples from the 7 hours cryomilled powders of 6061 Al and as received powders at the sintering conditions of 500°C–400°C/min–1.5 min.</table>

Advances in Materials Science and Engineering

fig6

Figure 6

Figure 6: Nanocrystalline 6061 Al Powder Fabricated by Cryogenic Milling and Consolidated via High Frequency Induction Heat Sintering 