Effect of Silicon Addition on High-Temperature Solid Particle Erosion-Wear Behaviour of Mullite-SiC Composite Refractories Prepared by Nitriding Reactive

Figure 1

XRD patterns of samples with different silicon powder addition nitridation sintered at 1500°C for 3 h.