Preparation of U–Zr–Mn, a Surrogate Alloy for Recycling Fast Reactor Fuel
Table 3
Material balance after injection casting of U–10 wt% Zr–5 wt% RE fuel slugs.
| | Casting part | Test | Test | Test | Mass (g) | Fraction (%) | Mass (g) | Fraction (%) | Mass (g) | Fraction (%) |
| Before casting | Crucible assembly | 607.2 | 100 | 428.1 | 100 | 420.19 | 100 | After casting | Crucible assembly | 497.1 | 81.86 | 362.3 | 84.62 | 365.0 | 86.90 | Mold assembly | 91.3 | 15.04 | 65.5 | 15.30 | 55.0 | 13.10 | Fuel loss | — | 18.8 | 3.10 | 0.30 | 0.06 | 0.19 | 0.04 |
|
|