Cyclic Stress Response and Fracture Behaviors of Alloy 617 Base Metal and Weld Joints under LCF Loading
Table 1
The chemical composition of Alloy 617 plate used in this study (wt.%).
| ā | ā | C | Ni | Fe | Si | Mn | Co | Cr | Ti | P | S | Mo | Al | B | Cu |
| ASTM | Min | 0.05 | Bal. | | | | 10.0 | 20.0 | | | | 8.0 | 0.8 | | | Spec. | Max | 0.15 | Bal. | 3.0 | 0.5 | 0.5 | 15.0 | 24.0 | 0.6 | 0.015 | 0.015 | 10.0 | 1.5 | 0.006 | 0.5 | Alloy 617 | 0.08 | 53.11 | 0.949 | 0.084 | 0.029 | 12.3 | 22.2 | 0.4 | 0.003 | <0.002 | 9.5 | 1.06 | <0.002 | 0.0268 |
|
|