Influence of Bottom Ash Replacements as Fine Aggregate on the Property of Cellular Concrete with Various Foam Contents
Table 3
Compressive strength, water absorption, and density of cellular concretes.
| Mixture | Compressive strength (MPa) | Water absorption (%) | Density (kg/m3) | 7 days | 14 days | 28 days | 7 days | 14 days | 28 days | 7 days | 14 days | 28 days |
| 30V0BA | 4.4 | 4.8 | 5.2 | 20 | 20 | 19 | 1336 | 1332 | 1296 | 30V25BA | 4.2 | 4.5 | 5.0 | 22 | 23 | 22 | 1270 | 1280 | 1165 | 30V50BA | 3.5 | 3.8 | 4.2 | 25 | 26 | 25 | 1248 | 1244 | 1241 | 30V75BA | 2.9 | 3.2 | 3.4 | 27 | 28 | 27 | 1180 | 1178 | 1171 | 30V100BA | 2.6 | 2.9 | 3.1 | 31 | 31 | 30 | 1141 | 1138 | 1142 |
| 40V0BA | 3.6 | 3.8 | 4.0 | 21 | 21 | 20 | 1184 | 1180 | 1176 | 40V25BA | 3.3 | 3.6 | 4.1 | 24 | 24 | 23 | 1151 | 1148 | 1142 | 40V50BA | 2.6 | 3.0 | 3.2 | 28 | 27 | 27 | 1112 | 1121 | 1118 | 40V75BA | 2.2 | 2.4 | 2.6 | 32 | 31 | 31 | 1065 | 1072 | 1068 | 40V100BA | 2.0 | 2.5 | 2.6 | 35 | 36 | 35 | 1012 | 1010 | 1008 |
| 50V0BA | 2.5 | 2.6 | 2.8 | 23 | 23 | 23 | 1064 | 1034 | 999 | 50V25BA | 2.5 | 2.7 | 2.8 | 28 | 27 | 28 | 1032 | 995 | 984 | 50V50BA | 1.8 | 2.0 | 2.3 | 35 | 34 | 34 | 1000 | 984 | 968 | 50V75BA | 1.6 | 1.7 | 1.9 | 37 | 35 | 36 | 924 | 883 | 856 | 50V100BA | 1.5 | 1.6 | 1.7 | 39 | 38 | 38 | 904 | 884 | 840 |
| 60V0BA | 1.7 | 1.8 | 2.0 | 26 | 26 | 27 | 960 | 892 | 832 | 60V25BA | 1.7 | 1.9 | 2.1 | 32 | 33 | 33 | 885 | 861 | 855 | 60V50BA | 1.4 | 1.4 | 1.6 | 38 | 38 | 37 | 832 | 835 | 827 | 60V75BA | 1.2 | 1.3 | 1.4 | 42 | 43 | 43 | 804 | 811 | 798 | 60V100BA | 1.1 | 1.1 | 1.2 | 45 | 46 | 46 | 766 | 755 | 762 |
| 70V0BA | 1.4 | 1.6 | 1.7 | 40 | 38 | 38 | 816 | 818 | 808 | 70V25BA | 1.5 | 1.5 | 1.7 | 42 | 42 | 44 | 795 | 791 | 797 | 70V50BA | 1.2 | 1.4 | 1.5 | 48 | 49 | 49 | 774 | 765 | 761 | 70V75BA | 0.9 | 1.0 | 1.0 | 52 | 53 | 53 | 740 | 738 | 735 | 70V100BA | 0.8 | 0.9 | 1.0 | 56 | 55 | 56 | 711 | 708 | 704 |
|
|