Effects of Nano-TiO2 on the Toughness and Durability of Cement-Based Material
Table 4
Internal pore distributions of hardened mortars at 28 days with different dosages of NT.
| Sample |
Total intruded volume/(mL/g) |
Mean radius/nm |
Apparent density/(g/cm3) |
Porosity/% (2 nm < < 5 μm) | Pore size distribution/% | <10 nm | 10–50 nm | >50 nm |
| M0 | 0.0685 | 13.85 | 2.385 | 15.6 | 3.74 | 10.30 | 1.56 | M1 | 0.0552 | 9.26 | 2.414 | 12.4 | 4.02 | 6.90 | 1.48 | M2 | 0.0426 | 7.84 | 2.459 | 11.9 | 4.64 | 5.95 | 1.31 | M3 | 0.0355 | 6.25 | 2.516 | 10.2 | 5.15 | 4.03 | 1.02 | M4 | 0.0573 | 9.56 | 2.402 | 13.1 | 3.98 | 7.61 | 1.51 | M5 | 0.0569 | 9.35 | 2.410 | 13.3 | 3.95 | 7.80 | 1.55 |
|
|