Physical and Mechanical Properties of Composites Made with Aluminous Cement and Basalt Fibers Developed for High Temperature Application
Table 1
Composition of studied composites.
| Basalt fibers (%) | Basalt aggregates (kg·m−3) | Fine components (kg·m−3) | Liquids (kg·m−3) | 0.0% | 0.25% | 0.5% | 1.0% | 2.0% | 4.0% | 0/4 mm | 2/5 mm | Cement Secar 71 | FGCP | Water | Plasticizer Sika 1035 | 0 (kg) | 7.25 (kg) | 14.5 (kg) | 29.0 (kg) | 58.0 (kg) | 116.0 (kg) |
| R-0 | A-0 | B-0 | C-0 | D-0 | E-0 | 880 | 220 | 900 | 0 | 224 | 22.75 | R-5 | A-5 | B-5 | C-5 | D-5 | E-5 | 880 | 220 | 855 | 45 | 224 | 22.75 | R-10 | A-10 | B-10 | C-10 | D-10 | E-10 | 880 | 220 | 810 | 90 | 224 | 22.75 | R-15 | A-15 | B-15 | C-15 | D-15 | E-15 | 880 | 220 | 765 | 135 | 224 | 22.75 | R-20 | A-20 | B-20 | C-20 | D-20 | E-20 | 880 | 220 | 720 | 180 | 224 | 22.75 | R-25 | A-20 | B-25 | C-25 | D-25 | E-25 | 880 | 220 | 675 | 225 | 224 | 22.75 |
|
|