Advances in Materials Science and Engineering / 2015 / Article / Fig 8

Research Article

Correlation of Grain Size, Stacking Fault Energy, and Texture in Cu-Al Alloys Deformed under Simulated Rolling Conditions

Figure 8

(a, b) Microstructure of Cu-2Al deformed to true axial strains of 0.5 in plane strain compression on the transverse section, for 70 μm and 250 μm, respectively.