Abstract

On the basis of the finite element calculation theory of electric field, the electric field distribution in a representative electrospinning device is computed. The electric field structure of a needle-plate type electrospinning device was simulated by means of ANSYS software. And the vector distribution of the nozzle on the spinneret pipe was got. For the purpose of the analysis on the influence of different solvent ratios on the performance of a single electrospun PVDF/PEI composite film, polyvinylidene fluoride and polyetherimide with a mass ratio of 8/2 were dissolved in a mixed solvent. The mixed solvent is composed of N,N-dimethylformamide and tetrahydrofuran, added in different proportions. Through the electrostatic spinning technology, PVDF/PEI composite fiber membranes were prepared. Using scanning electron microscopy (SEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), and mechanical properties testing, the effects of tetrahydrofuran on the composite microstructure, crystallinity, and mechanical properties of the PVDF/PEI composite fiber membranes are discussed.

1. Introduction

Electrospinning is a procedure of generating continuous nanofibers using polymer solutions in the presence of an electric field [13]. Nanofibrous nonwovens, because of interconnected pores and a large surface-to-volume ratio, enable many applications of these structures in the field of filtration media, medicine, and industry [4, 5]. It is crucial to simulate the electric field distribution of an electrospinning device [69]. For electrospinning, a metallic capillary with a high voltage DC is joined to a container, which is filled with a polymer solution [10, 11]. When the electric field force is higher than the surface tension of the polymer solution, a thin jet is formed in the capillary nozzle. Figure 1 is a schematic illustration of an electrospinning experimental system. The distribution of electric field directly influences the fineness and morphology of the electrospun fiber [1216]. The polyvinyl chloride insulating tubes are used to form a unified and centralized electric field [7]. COMSOL multiphysics software was employed to simulate and analyze the value and distribution of the electric field strength during a multineedle electrospinning process [2]. The metal needle length under the metal plate electrode is changed to create different electric field distributions [8]. Electric field distribution of the multijet spinning device is improved [17]. A new electrospinning configuration with a 19-hole multistep has been demonstrated [18]. Other related studies on electrospinning are given in [1922]. Electric field distribution affects fiber alignment and further affects the performance of electrospun composite film. Consequently, it is crucial to simulate the electric field distribution in an electrospinning device and to analyze the effect of different solvent ratios on the performance of a single electrospun PVDF/PEI composite film.

2. Computational Principles of Electric Field

2.1. Potential Function

Assuming that the potential function of each triangular mesh element is linear for the variables and in the cylindrical coordinate, then the electric field is perceived as approximate homogeneous in each triangular mesh element domain. So, the potential of every point of each triangular mesh element follows such a rulewhere , , and are the coefficients and and are the distance between the center of triangular mesh element to -axis and the coordinate value of the center of the triangular mesh element along with -axis, respectively.

, , and represent node numbers of single triangular mesh element, respectively. Therefore,where

The area of triangular mesh element is as follows:

Hence, the interpolating functions of triangular mesh element can be expressed as

2.2. Energy Function of Triangular Mesh Element

Energy function of triangular mesh element is as follows:where is the dielectric constant of triangular mesh element .

According to (3), we know that ; that is, and of each point in triangular mesh element are both constant. And they are not affected by coordinate value . Therefore, simplified is as follows:where represents the distance between the center of triangular mesh element and -axis.

Therefore,

2.3. Calculation of the Electric Field

Electric field strength is as follows:

and are -component and -component of the electric field strength, respectively:

Its absolute value is

3. Electric Field Simulation of Needle-Plate Type Electrospinning Machine

3.1. Finite Element Analysis (FEA) of Electric Field

On the basis of the -method for the FEA of the electric field [2, 3], using ANSYS software, we proposed some assumptions: (1) the dielectric constant, which is not affected by the electric field, is definite value; (2) electrification of the spinning fiber has no influence on the electric charge; (3) the control system has no influence on the electric field distribution; (4) the volume density of the field electric charge is . By comparing with different kinds of mesh element, eight nodal points PLANE121 are selected. Figure 2 is a simplified FEA mesh model using ANSYS software. Table 1 shows the parameters setting.

3.2. Simulation Result of the Electric Field

The vector distribution of the electric field, which has an axial symmetric characteristic, is shown in Figure 3. Figure 4 shows that the peak of the electric field intensity appears at the spinning pipe orifice, and the direction of the electric field points to the negative plate. The peak of the electric field intensity is . Influence of the collecting distance on the electric field intensity is shown in Figure 5. We determined that the field intensity suddenly went down to the minimum value, particularly at a near distance with spinneret pipe orifice.

4. Electrospinning Experiment

4.1. Reagent

PVDF (Arkema SA, Mw = 3 × 105) and PEI (GE Ultem-1000) were used without further purification to prepare the electrospun fibrous materials. N,N-Dimethylformamide (DMF, >99.5%), absolute ethanol, and tetrahydrofuran (THF) were purchased from Tianjin Fu Yu Hua Gong Co., Ltd.

4.2. Electrospinning Experimental System

Figure 6 is the electrospinning experimental system. The high voltage DC power supply, fabricated at the Electrical Engineering Department of Tsinghua University, can be continuously adjusted between 0 V and 100 KV. In order to avoid the influence on the input signal, the electrospinning experimental system chooses shielded cable as the connecting line.

4.3. Preparation of PVDF/PEI Composite Fiber Membrane

To prepare the electrospinning solution with a mass fraction of 18%, the polymer with a mass ratio of m(PVDF)/m(PEI) = 8/2 was dissolved in the mixed solvent, with m(DMF)/m(THF) of 9/1, 8/2, 7/3, 6/4, and 5/5. At room temperature 20°C, the electrospinning process parameters are set to the static voltage 16 KV and the flow rate is 0.1 mL/h. A static collecting device was used. The distance, which is between the nozzle and the collecting device, is 20 cm. The thickness of the PVDF/PEI composite fiber membrane was controlled to 40–80 μm. The finished PVDF/PEI composite fiber membrane is thermally treated at 80°C for 12 h, and then it is packed until used.

4.4. Scanning Electron Microscopy (SEM)

After spraying the sample, the surface microscopic morphology of the PVDF/PEI composite fiber membrane was observed using a FEI Sirion200 SEM (Philips Corporation, Netherlands).

4.5. X-Ray Diffraction (XRD)

The composite fiber membranes were tested by XRD (PANalytical Corporation, Netherlands). The diffraction patterns of the composite fiber membranes were analyzed using a Cu(K) target. The tube voltage was 40 KV, and the tube current was 50 mA. The scanning speed is 1°/min over the scanning angle range of 5° to 80°, with a step length of 0.02°.

4.6. Differential Scanning Calorimetry (DSC)

Thermal properties of the composite fiber membrane are measured under N2 using DSC. The initial temperature was 40°C, and the composite fiber membranes were heated to 250°C at the rate of 10°C/min. Through the change in the height of the endothermic peak, the area under the endothermic peak and the enthalpy value and the influence of the crystallinity of the fiber membrane on the mechanical properties are analyzed. The crystallinity can be calculated as follows:where is the melting enthalpy of the samples and is the melting enthalpy of the fully crystallized PVDF (104.7 J/g).

4.7. Mechanical Properties

The tensional strength and elongation ratio of the composite fiber membrane are tested using the AGS-J electronic universal testing machine (Shimadzu Corporation, Japan), according to the standard of the 11th chapter of 13542.2-2009 GB/T. The finished composite fiber membrane was cut to a length of 10 cm and a width of 1 cm, and the distance between the fixtures was 100 mm. The tensile test is performed at a tensile rate of 5 mm/min along the direction of the sample length. The tensile strength can be calculated as follows:where is the tensile strength, is the sample load, and is the cross-sectional area. Each composite fiber membrane has three samples, and the average value is taken.

5. Discussion

5.1. Surface Topography

From the SEM photo of the PVDF/PEI composite fiber membrane at 5000x magnification, which is shown in Figure 7, it can be clearly seen that with the increase in the proportion of THF the morphology of the fibers is obviously different. When the solvent mass ratio m(DMF)/m(THF) is 9/1, the fibers intertwist, and the fibers have more cross-linking branches, as shown in Figure 7(a). The morphological uniformity decreases because the volatility of THF and DMF is different, and when the THF content is less, the electrospinning solution has poor volatility. Under the influence of the electric field force, THF volatilizes rapidly. This causes the jet to solidify into fibers at a slower rate, and the jet has not yet solidified after deposition in the collection device, and the nonsolidified fibers are dissolved in the residual solvent, which causes the phenomenon of intertwist between the fibers. When the solvent mass ratios of m(DMF)/m(THF) are 8/2, 7/3, and 6/4, with an increase in the THF content in the solvent system, the solvent volatility increases, the surface tension of the solution decreases, and the volatile component (THF) in the mixed solvent increases. This is beneficial to the formation and consolidation of PVDF/PEI fibers. As can be seen from Figures 7(b), 7(c), and 7(d), the PVDF/PEI composite fiber membranes are typical interpenetrating microporous structures with no droplets or bead defects. When the solvent mass ratio m(DMF)/m(THF) is 7/3, the fiber diameter distribution is relatively uniform. In Figure 7(e), when the solvent mass ratio m(DMF)/m(THF) is 5/5, the beads appear on the fibers, and the fiber diameter distribution is relatively wide. This is because when the volatile solvent (THF) content is too large, the solution can volatilize easily, so it is difficult to form a Taylor cone at the nozzle. It is not easy to form a stable electrospinning jet, and the molecular chain is short and not sufficient for entanglement. So this will cause the formation of beads on the fiber.

5.2. XRD Analysis

Figure 8 shows the X-ray diffractogram of PVDF/PEI composite fiber membranes prepared by electrospinning with different solvent ratios. In the diffractogram of the PVDF powder sample without electric field polarization, there are obvious characteristic peaks at a diffraction angle of 27°, which corresponds to the phase and belongs to the monoclinic system. However, the corresponding curve for the PVDF/PEI composite fiber membrane with different solvent ratios prepared by electrospinning becomes flat and even disappears compared to the peak at 27°. This shows that the crystal form of the PVDF/PEI composite fiber membrane gradually decreases compared to the pure PVDF fiber membrane. In addition, compared to the pure PVDF powder, the PVDF/PEI composite fiber membrane shows peaks at 37°and 42°, which correspond to the and phases, respectively. However, these two characteristic peaks are very weak in pure PVDF powder. Although the intensity of the two peaks in the PVDF/PEI composite fiber membrane is not very high, it can be attributed to the change in the crystal form of PVDF during electrospinning. The crystal form is transformed into the and crystal forms, increasing their content in the PEI/PVDF composite fiber membrane. Under the influence of the polarized electric field, the PVDF will produce a phase transition from to . The reason for the transformation from nonpolar to the polar crystal phase is the orientation of the dipole charge along the electric field direction, the rotation of the PVDF molecular chain, and the orientation of the intrinsic dipole, which leads to the full trans-planar zigzag conformation, changing the PVDF crystal type.

5.3. DSC Analysis

The DSC curves of different solvent ratio PVDF/PEI composite fiber membranes prepared by electrospinning are shown in Figure 9, and the thermal properties and the crystallinity are shown in Table 2.

The melting point of PVDF is about 170°C, so this material, which is reflected by the endothermic peak, is the PVDF fiber. The initial, end, and the peak position of the endothermic peak are located within the allowable error scope. Table 2 shows the thermal properties and the crystallinity of different solvents ratio PVDF/PEI composite fiber membrane prepared by electrospinning. The melting point of the PVDF/PEI composite fiber membrane with different solvent ratios prepared by electrospinning did not change. However, with an increase in the proportion of THF, the crystallinity of the PVDF/PEI composite fiber films increased first and, then, decreased. When the mass ratio of DMF/THF was 7/3, the crystallinity was 31.27. This shows that under the electric field force crystallization changes are more likely to occur in PVDF because of the interaction of the dipole and the effect of the hydrogen bond of the chain between the DMF molecule, THF molecule, and PVDF. However, with the increase in the content of the volatile solvent, THF, the spinning solution became stronger. When the THF content is too large, it leads to instability of the jet and a decrease in the crystallinity of the PVDF/PEI composite fiber films.

5.4. Mechanical Properties Analysis

The mechanical properties of different solvent ratio PVDF/PEI composite fiber membranes prepared by electrospinning are shown in Figure 10. With the increase in the THF content, the fracture stress and elongation at break first increase and, then, decrease. When the m(DMF)/m(THF) is equal to 7 : 3, the fracture stress and elongation at break of the composite fiber membranes reach the maximum values of 4.778 MPa and 23.5327%, respectively. This is because the solution forms a jet during the process of electrospinning, and the polymer molecular chain opened in the solvent is highly stretched by the electric field force. The polymer molecular chain is oriented and arranged again. With the evaporation of the solvent, the jet is solidified forming polymer fibers. Under the condition of invariable electrospinning parameters, when the THF content is less in the mixed solvent, the electrospinning solution has poorer volatility. This affects the phase separation of the solution in the process of jet stretching and, then, results in a decrease in the orientation and poorer mechanical properties of the polymer molecular chain. When the THF content is more in the mixed solvent, the electrospinning solution has better volatility. However, under the electric field force during electrospinning, it is unable to form a stable jet; the polymer molecular chains cannot entangle, resulting in a decrease in the mechanical properties of the polymer molecular chain.

6. Conclusions

PVDF is widely used because of its good properties, such as resistance to chemical corrosion and weatherability. PVDF/PEI composite fiber membranes were prepared using electrospinning and the properties of different solvents ratio PVDF/PEI composite fiber membranes were tested. The conclusions are as follows:(1)On the basis of the finite element calculation theory of electric field, the electric field distribution in a representative electrospinning device is computed. The electric field structure of a needle-plate type electrospinning device was simulated by means of ANSYS software. And the vector distribution of the nozzle on the spinneret pipe was got.(2)SEM images show that when the THF ratio is too small or too large, the electrospinning solution is too slow, and the jet is still not solidified after deposition on the collection device, making it easy to form fiber bonding. When the electrospinning solution volatilized easily, it is difficult to form the Taylor cone at the nozzle, which is not conducive to form the fiber.(3)X-ray diffraction analysis shows that under the influence of an electric field force the crystal form is transformed from into and forms, and the PVDF with the crystal form has a strong ferroelectric effect during electrospinning. Therefore, it is expected that the PVDF/PEI nanometer composite material with ferroelectric function can be obtained by electrospinning. DSC curves show that under certain electrospinning parameters the volatility of the electrospinning solution has some influence on the orientation and alignment of the polymer molecular chains under the electric field force.(4)Mechanical test results show that with the increase in the THF content the fracture elongation and the fracture stress of PVDF/PEI first increase and then decrease. When the solvent mass ratio was m(DMF)/m(THF) = 7 : 3, the fracture stress and the fracture elongation of the composite electrospinning fiber films are maximum. This is because the increase in the THF content leads to an increase in the volatility of the spinning solution. Under the action of the electric field force, the molecular chain structure is improved, and the mechanical properties are improved. However, when the THF content is too large, the jet becomes unstable, which is not conducive to form fibers, and the mechanical properties decrease. These agree well with the DSC results.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

This work is supported by Heilongjiang Postdoctoral Funds for Scientific Research Initiation (Grant no. LBH-Q13093), Science Funds for the Young Innovative Talents of HUST (Grant no. 201509), and Harbin Science and Technology Innovation Researchers Project (Grant no. 2012RFJGG013).