Properties of a Laminated Wood Composite Produced with Thermomechanically Treated Veneers

Table 4

Mechanical properties of plywood made from thermomechanically treated veneers.

Material
	N/mm^2				N
Control	8604	81.1	40.2	3.35	4054
140°C, 1 min, 2.7 N/mm^2	8704	81.7	42.6	3.88	4882
140°C, 2 min, 2.7 N/mm^2	9300	86.2	41.5	4.08	4704
180°C, 1 min, 2.7 N/mm^2	9036	84.0	42.9	4.03	4869
180°C, 2 min, 2.7 N/mm^2	9654	80.9	43.6	4.72	4610

Significant difference between control and treatment at 0.05 level by Dunnett’s test. : bending modulus of elasticity; : bending strength; : parallel compression strength; : glue line shear strength; : Janka hardness.