DSC analysis of WF 50 PLA composite at cycle 0 and cycle 6.
| Properties | Cycle 0 | Cycle 6 |
| Melting point (°C) | 152.15 | 149.64 | Crystallization temperature (°C) | 145.33 | 144.24 | Heat of fusion (J/g) | 16.64 | 15.42 | Crystallinity (%) | 38.03 | 35.24 |
|
|