Durability of Mortar Made with Fine Glass Powdered Particles
Table 1
Physical and chemical characterization of colorless and amber glass microparticles.
| Item | Colorless | Amber |
| Insoluble residue (%) | 92.72 | 94.39 | Loss on ignition (%) | 0.22 | 0.37 | Silicon dioxide | 73.93 | 72.95 | Calcium oxide | 9.18 | 9.28 | Aluminium oxide | 0.25 | 0.82 | Ferric oxide | 0.92 | 0.66 | Magnesium oxide | 3.75 | 3.58 | Sulphur trioxide | 0.23 | 0.25 | Sodium oxide | 9.18 | 5.99 | Potassium oxide | 0.02 | 0.02 | Alkali equivalent (%) | 9.19 | 6.00 | Specific mass (g/cm3) | 2.60 | 2.54 | Specific surface, BJH (m2/kg) | 4.265 | 4.918 | Specific surface, Blaine (m2/kg) | 371.8 | 366.3 |
|
|