The Effects of Humidity on Cast PA6G during Turning and Milling Machining
Table 1
The physical properties of the cast PA6G material.
| Properties | Unit | Value |
| Specific gravity | g/cm3 | 1.15 | Service temperature | °C | 100 | Melting point | °C | 190 | Thermal elongation | 1/K105 | (8-9)10−5 | Tensile strength | MPa | 55–85 | Rapture strength | MPa | 88–90 | Elongation at break | % | 10–40 | Modulus of elasticity | MPa | 3900–4200 | Water absorption | % | 6-7 | Volumetric resistance | W·cm | >1015 | Surface resistance | | >1012 | Dielectric strength | kV/mm | 80–100 | Rockwell | scala | M88 | Ball notch 358/30 | MPa | 110–160 |
|
|