In Situ Catalytic Pyrolysis of Low-Rank Coal for the Conversion of Heavy Oils into Light Oils

Amin, Muhammad Nadeem; Li, Yi; Lu, Xingmei

doi:https://doi.org/10.1155/2017/5612852

Advances in Materials Science and Engineering

On this page

Abstract Introduction Results and Discussion Conclusions Acknowledgments References Copyright Related Articles

Research Article | Open Access

Volume 2017 | Article ID 5612852 | https://doi.org/10.1155/2017/5612852

In Situ Catalytic Pyrolysis of Low-Rank Coal for the Conversion of Heavy Oils into Light Oils

Muhammad Nadeem Amin,¹Yi Li,¹and Xingmei Lu¹

Academic Editor: Faheem K. Butt

Received18 Aug 2016

Accepted27 Sept 2016

Published22 Jan 2017

Abstract

Lighter tars are largely useful in chemical industries but their quantity is quite little. Catalytic cracking is applied to improve the yield of light tars during pyrolysis. Consequently, in situ upgrading technique through a MoS₂ catalyst has been explored in this research work. MoS₂ catalyst is useful for the conversion of high energy cost into low energy cost. The variations in coal pyrolysis tar without and with catalyst were determined. Meanwhile, the obtained tar was analyzed using simulated distillation gas chromatograph and Elemental Analyzer. Consequently, the catalyst reduced the pitch contents and increased the fraction of light tar from 50 to 60 wt.% in coal pyrolysis tar. MoS₂ catalyst increased the liquid yield from 18 to 33 (wt.%, db) and decreased gas yield from 27 to 12 (wt.%, db) compared to coal without catalyst. Moreover, it increased H content and hydrogen-to-carbon ratio by 7.9 and 3.3%, respectively, and reduced the contents of nitrogen, sulphur, and oxygen elements by 8.1%, 15.2%, and 23.9%, respectively, in their produced tars compared to coal without catalyst.

1. Introduction

Coal is heterogeneously complex structure having organic and inorganic macromolecules. Low-rank coals have great importance in utilization but have some problems due to low efficiency and higher CO₂ emissions compared to high-rank coals. These coals are difficult for storage and transportation and are not suitable for direct combustion [1–5]. The utilization of a low-grade coal could be achieved through pyrolysis which converts the coal volatiles into high valuable fuels and fine chemicals. A coal tar in bulk quantity is produced during pyrolysis, but it contains high range of heavy organic components having boiling point greater than 360°C called pitch. The high boiling point range organic components are not easy to be treated since they can easily precipitate in the pipelines with dusts, so they will create problems during operation of downstream equipment like engines and turbines and block the pipelines in the industry. High valuable tar can be achieved to crack high range organic heavy components into desired components having boiling point less than 360°C. However, the thermal cracking of tar generally occurs at high temperature through appropriate energy supply and reaction time which leads to decreasing the energy efficiency and tar yield. So, the catalytic coal pyrolysis is the most promising technique to upgrade the coal pyrolysis tar under moderate conditions and increase the energy efficiency of industrial equipment [6–21].

To improve the tar yield and fraction of light components in coal tar, catalytic coal pyrolysis experiments have been performed through mixing or without mixing of coal with catalysts in previous study [22–31]. Li et al. [25] were reported to improve aromatic components yield like BTEXN on zeolite catalysts. Liu et al. [26] studied improving the yield of tar over Ni-MgO and obtained the higher tar yield, when the coal during pyrolysis was incorporated to CO₂ for reforming methane. Jin et al. [27] studied improving the tar yield on zeolite catalyst (Mo-HZSM-5) for integrating the aromatization of methane during coal pyrolysis and obtained yield of coal tar about 21.5% at the pyrolysis temperature of 700°C. Li et al. [28] investigated the long flame Huang Tu Miao coal over different catalysts (NaX, CoO, MoO, and CoO-MoO) and enriched CO, CH₄, and aromatic components formation with NaX zeolite catalyst. Ma et al. [29] studied five Chinese coals with mechanical mixing of catalyst and coals on catalytic hydropyrolysis to represent the increase in liquid yield with a small influence on BTX yield over ZnCl₂ and MoS₂ improved BTX and gases yield. Li et al. [30] explored the product analysis of impregnated lignite coal with sulphided molybdenum catalyst and exhibited increment in yield of tar up to about 63.9% as well as light aromatics such as BTX, phenol, cresol, and xylenol (PCX), and naphthalene also increased during the catalytic multistage hydropyrolysis (MHyPy) as compared to the traditional hydropyrolysis. The preceding studies for enhancing the coal pyrolysis tar are generally under hydrogen and pressure conditions [31, 32], while their large observations have been dedicated to the differences of specific components like BTEXN.

In foregoing work, mechanical mixing and impregnation of MoS₂ catalyst with lignite coals were applied on the basis of research aims during catalytic hydropyrolysis [29, 30]. Thus, low-grade coal in this research’s aim and MoS₂ catalyst were used separately in a dual-stage reactor having two sections through atmospheric pressure for the enhancement of coal pyrolysis tar. Moreover, the catalytic effect of MoS₂ on coal tar quality in terms of distilled temperature difference was investigated and also the behavior of catalytic upgrading in the conversion of heavy tar components was studied.

2. Experimental Portion

2.1. Synthesis of Raw Coal and Catalyst

Low-rank Shengli coal was grounded to the required size (20–40 mesh) for testing of experiments. Table 1 shows the results of raw Shengli coal. Raw coal was held for drying overnight at 120°C before each testing. A material MoS₂ (≥98%) as a catalyst supplied by Sinopharm Chemical Reagent Co., Ltd., was selected and amount of MoS₂ catalyst (2.5 g) was used in each experiment. The powder MoS₂ material was heated at 120°C and then calcined at 500°C within 4 h. It was pelletized with machine (769YB-24B) at 10 MPa pressure and then sieved to particle size of 20–40 meshes.

2.2. Testing Method

The testing section consisted of gas supply, a dual-stage fixed bed reactor, electric ring furnace, and tar and gas collection system as shown in Figure 1 as reported in our last research [33]. It was prepared through glass tube containing three parts including upper section, lower section, and a cover. The upper section containing a porous sintering quartz plate was used for the coal pyrolysis having 30 mm inner diameter and 200 mm length. The lower section was adopted for primary products during pyrolysis having 34 mm inner diameter and 550 mm length. Both parts were externally heated by an electric ring furnace. Two K-type thermocouples were kept inside the reactor for temperatures such as pyrolysis and cracking.

High purity N₂ carrier gas (Beiwen, Beijing, China, 99.99%) was controlled with a mass flow meter. It gave pyrolysis initial reaction in the dual-bed reactor. A 5 g coal was kept in the upper part of the pyrolysis and 2.5 g catalyst was kept in lower part of the catalytic upgrading of coal. The pyrolysis products from the upper section were transformed and go through the catalyst bed in lower part. Finally, obtained product was passed through condenser; it was cleaned with acetone thoroughly to get coal pyrolysis tar. Noncondensable pyrolysis gases were dewatered through calcium chloride block and received in gas bags. All pipelines were cleaned using acetone and then the liquid was obtained. The obtained liquid (acetone plus water) including tar was first dehydrated with MgSO₄. It was kept on filter paper for filtration and the acetone was removed at 30°C in a rotary machine to get coal pyrolysis tar.

The experiments represented that reaction can finish within about 40 min during pyrolysis. The testing methods for coal with and without catalyst were as follows. A 5 g coal was pyrolyzed without catalyst in the upper part through electric furnace. It was performed for heating the coal through a temperature controller with 100°C per minute to 600°C temperature. Coal (5 g) was pyrolyzed and catalyst (2.5 g) was also put in lower part during upgrading of coal pyrolysis tar. Both parts were heated with a rate of 100°C per minute at 50 mL per min of gas flow from ambient to 600°C temperature. Both pyrolysis and cracking temperatures were kept within 30 min at 600°C. All performed tests were repeated three times and average was calculated as the final reading.

2.3. Coal Derived Products and Catalyst Analysis

Noncondensable and hydrocarbon gases were measured through a gas chromatograph as described in our last work [33]. The coal pyrolysis tar having aromatic and hydrocarbons was measured through analysis equipment as reported in our last study [33]. The boiling point range less than 360°C refers to the light tar and heavy tar having more than 360°C.

The catalyst characterization was analyzed through X-ray pattern machine and micropore analyzer as described in our last article [33]. The catalyst morphology was seen through scanning electron microscopy (SEM) with a JOEL machine (JSM-6700F) and transmission electron microscopy (TEM) was adopted to measure the catalyst with a JOEL (JEM-2100F).

Coal tar yield (), lighter tar fraction (), lighter tar yield (), noncondensed pyrolysis gas yield , gas yield , char yield , and liquid yield were calculated using (1) to (7) for the distribution of pyrolysis products.

Tar yield is given as follows:

Light tar fraction is given as follows:

Light tar yield is given as follows:

Pyrolysis gas yield is given as follows:

Gas yield is given as follows:

Char yield is given as follows:

Liquid yield is given as follows:, , , , , and represent the masses of raw coal, tar, light tar, noncondensed pyrolysis gas components, pyrolysis gas, and char in grams, respectively, and in shows the pyrolysis components of gas.

3. Results and Discussion

3.1. Temperature Influence on Coal without Catalyst

Coal having tar yield from 300 to 700°C is shown in Figure 2. It determined the suitable temperature that led to the maximum tar yield. More volatile matters were released at more than 600°C temperature and moved towards large cracking reactions to reduce coal tar yield during pyrolysis. Therefore, the temperature 600°C was selected. The product yields including gas, liquid, and char during coal pyrolysis without catalyst are depicted as in Figure 3. It can be stated that increase in gas yield occurred with the temperature from 300 to 700°C. The gas yield was increased which might be due to evolution of micro compounds due to the secondary tar reactions and large amount of volatiles was achieved at 600°C during pyrolysis. It was also observed that liquid yield increased from 300 to 400°C and then decreased. The reduction in liquid yield from 500 to 700°C indicates high reaction rates during decomposition. The expression of increase and reduction in liquid yield with temperature was reported in literature [34, 35]. The declining in char yield occurred from 300 to 500°C and then became stable above 500°C temperature. The stability of char yield above 500°C showed the complete burning of coal during pyrolysis. The temperature more than 600°C is attributed to the increment of gas yield and reduction in coal tar yield.

3.2. Catalyst’s Influence on Pyrolysis Product Yields

The catalyst having influence on yield of pyrolysis products during coal pyrolysis is described in Figure 4. It can be noted that the increment in liquid yield from 18 to 33 (wt.%, db) occurred due to catalytic effect during coal pyrolysis. The liquid yield increment might be due to high condensation reaction during catalytic coal pyrolysis, while gas yield decreased from 27 to 12 (wt.%, db) after catalysis and char yield (55 wt.%, db) remained constant before and after catalyst. These results showed that decrease in gas yield might be due to the catalytic effect on the released volatiles during coal pyrolysis. The liquid yield increment and gas yield reduction with the catalyst were studied in literature [31].

3.3. Gas Composition without and with Catalyst during Coal Pyrolysis

Pyrolysis gas components and hydrocarbon gases () without and with catalyst are shown in Figure 5. It can be thought that gas components yield declined after catalysis. The pyrolysis of low-rank coal produces rich oxide of carbon due to large content of oxygen in raw material. The pyrolysis gases can provide energy requirement for plant during pyrolysis due to high content of carbon oxides [36]. The yields of gas components (H₂, CH₄, and CO) generated through the condensation reactions, whereas the yield of CO₂ was produced due to the cracking of carboxyl group from coal during pyrolysis [37]. Thus, carbon oxide gases also decreased after catalysis. Therefore, the catalyst might be catalyzing the forward and reverse water gas reactions, which are attributed to declining gas yields.

3.4. Tar Characterization

Tar fraction as a function of simulated distillation temperature without and with catalyst is shown in Figure 6. It is noted that initial and final temperatures of tar decreased after catalysis which indicated that tar evaporated rapidly. These results showed that the amount of light weight tars was higher than that without catalyst. The composition of tar before and after catalyst during pyrolysis is shown in Figure 7. The light weight tars fraction increased after catalysis; meanwhile the variations of wash and anthracene oils fractions were small. The pitch was also decreased after catalysis. For all compared data, the pyrolysis temperature in the upper layer was 600°C, the adopted catalyst was 50 wt.% of the pyrolyzed coal, and the cracking temperature was 600°C. Moreover, it is clear from Figures 5 and 6 that the catalyst had ability to produce more light weight tars during pyrolysis.

The tar yield, light tar fraction, and yield are represented in Figure 8. In this case, the fraction of light tar is the sum of all oil components in Figure 7 except pitch. Moreover, it can be seen that the light tar fraction increased from 50 to 60 wt.% for the secondary upgrading over MoS₂ catalyst. The results showed that the secondary upgrading had greatly enhanced the overall tar quality, so that the downstream treatment could become more efficient and easier. In comparison to the coal pyrolysis without catalyst, the light tar yield with the catalyst increased significantly. It can be considered from light tar yield and fraction that MoS₂ catalyst might have the best upgrading effect. The elemental analysis data of tar before and after catalyst is shown in Table 2. The coal pyrolysis with catalyst increased hydrogen-to-carbon ratio and also reduced nitrogen, sulphur, and oxygen elements in coal pyrolysis tar. After the catalysis, tar yield is declined, while hydrogen and hydrogen-to-carbon ratio are increased as 7.9 and 3.3%, accordingly. Overall, MoS₂ catalyst was highly efficient in producing lighter coal pyrolysis tar fraction, upgrading the coal tar products, and reducing the pitch contents in coal pyrolysis tar.

3.5. Catalyst Characterization

The XRD pattern of MoS₂ catalyst is shown in Figure 9. A detailed view of diffraction peaks of the catalyst showed the formation of single-phase molybdenum sulfide (MoS₂) hexagonal structure as indicated by the index at 14.4°, 32.7°, 39.6°, 44.3°, 49.8°, and 60.4° corresponding to the (002), (100), (103), (104), (105), and (112) crystal planes, respectively. The entire XRD diffraction pattern was attributed to exhibit pure MoS₂ hexagonal form, which had well adjustment to the values as shown (JCPDS 65-1951). XRD pattern represented no other peaks, exhibiting pure form of MoS₂ material. The strong and clear diffraction peaks showed that MoS₂ material is highly crystalline. The highest intensity peak in the diffraction peaks shows high crystal formation.

The porosity of fresh and spent catalysts was calculated from nitrogen adsorption/desorption isotherms. The BET surface areas of the fresh and spent catalysts are 3 and 5 m²g⁻¹, respectively, and there was no significant difference between fresh and spent catalysts. The volume of pore in spent catalyst increased from 0.015 to 0.025 cm³/g, while pore diameter was reduced from 23.65 to 16.66 nm. It is realized that BET surface area and volume of pore increment might be attributed to the breakdown of pore which was suffered from high volatiles during pyrolysis and the cracking of coal pyrolysis tar.

The surface structure of fresh and spent catalysts with high magnification is shown in Figures 10(a) and 10(b). From Figures 10(a) and 10(b), it can be seen that both catalysts were composed of MoS₂ platelets. Figure 10(a) shows MoS₂ crystals in the form of platelets. After the reaction, the MoS₂ platelets formed a large lump which might be due to high temperature and upgrading the coal pyrolysis tar during pyrolysis. TEM diagrams of both catalysts (fresh and spent) are shown in Figures 11(a) and 11(b), respectively. From Figure 11(a), it is noted that the catalyst had nanoscale layer on its structure. The nanoscale accumulated phenomenon reduced the edge surface of the catalyst. It showed that sulphur atoms had strong molybdenum adsorption on the surface of the edges, while molybdenum had strongly adsorbed sulphur atoms. After the reaction, the edges on the surface of the catalyst reduced and changed into small nanolayers. The formation of small nanolayers after the reaction might be due to high temperature and decomposition of the coal pyrolysis tar during catalytic coal pyrolysis. Moreover, TEM showed highly crystalline material; its size was around 100 nm.

(a)

(b)

(a)

(b)

4. Conclusions

It was testified that MoS₂ catalyst was able to increase liquid product yield and produced the highest liquid yield. Moreover, it is found that the catalyst decreased the pitch in the tar and showed the increment in the lighter weight tars fraction. Therefore, the catalyst was also active for the increment in hydrogen-to-carbon ratio and reduction in nitrogen, sulphur, and oxygen elements in coal pyrolysis tar. The catalyst in this study was more effective to upgrade the coal pyrolysis tar to decompose the coal catalytically, although MoS₂ catalyst can promote the energy efficiency during the operation of industrial equipment.

Competing Interests

The authors declare that they have no competing interests.

Acknowledgments

In this research study, authors acknowledge gratefully the funding support of Beijing Natural Science Foundation (no. 3142020), Strategic Priority Research Program of CAS (no. XDA07010300), CAS Province Cooperation Program (no. 2014JZ0012), and National Major Instrumentation Development (no. 2011YQ12003907).

References

N. Wang, J. Yu, A. Tahmasebi et al., “Experimental study on microwave pyrolysis of an Indonesian low-rank coal,” Energy & Fuels, vol. 28, no. 1, pp. 254–263, 2014.
View at: Publisher Site | Google Scholar
J. Yu, A. Tahmasebi, Y. Han, F. Yin, and X. Li, “A review on water in low rank coals: the existence, interaction with coal structure and effects on coal utilization,” Fuel Processing Technology, vol. 106, pp. 9–20, 2013.
View at: Publisher Site | Google Scholar
A. Tahmasebi, J. Yu, Y. Han, F. Yin, S. Bhattacharya, and D. Stokie, “Study of chemical structure changes of chinese lignite upon drying in superheated steam, microwave, and hot air,” Energy and Fuels, vol. 26, no. 6, pp. 3651–3660, 2012.
View at: Publisher Site | Google Scholar
M. Karthikeyan, W. Zhonghua, and A. S. Mujumdar, “Low-Rank coal drying technologies—current status and new developments,” Drying Technology, vol. 27, no. 3, pp. 403–415, 2009.
View at: Publisher Site | Google Scholar
C. Bergins, S. Berger, and K. Strauß, “Dewatering of fossil fuels and suspensions of ultrafine particles by mechanical/thermal dewatering,” Chemical Engineering and Technology, vol. 22, no. 11, pp. 923–927, 1999.
View at: Publisher Site | Google Scholar
J. Han, X. Wang, J. Yue, S. Gao, and G. Xu, “Catalytic upgrading of coal pyrolysis tar over char-based catalysts,” Fuel Processing Technology, vol. 122, pp. 98–106, 2014.
View at: Publisher Site | Google Scholar
X. Qu, P. Liang, Z. Wang et al., “Pilot development of polygeneration process of circulating fluidized bed combustion combined with coal pyrolysis,” Chemical Engineering & Technology, vol. 34, no. 1, pp. 61–68, 2011.
View at: Publisher Site | Google Scholar
J. Wang, X. Lu, J. Yao, W. Lin, and L. Cui, “Experimental study of coal topping process in a downer reactor,” Industrial and Engineering Chemistry Research, vol. 44, no. 3, pp. 463–470, 2005.
View at: Publisher Site | Google Scholar
T. Kimura, T. Miyazawa, J. Nishikawa et al., “Development of Ni catalysts for tar removal by steam gasification of biomass,” Applied Catalysis B: Environmental, vol. 68, no. 3-4, pp. 160–170, 2006.
View at: Publisher Site | Google Scholar
S. J. Juutilainen, P. A. Simell, and A. O. I. Krause, “Zirconia: selective oxidation catalyst for removal of tar and ammonia from biomass gasification gas,” Applied Catalysis B: Environmental, vol. 62, no. 1-2, pp. 86–92, 2006.
View at: Publisher Site | Google Scholar
P. Liang, Z. Wang, and J. Bi, “Process characteristics investigation of simulated circulating fluidized bed combustion combined with coal pyrolysis,” Fuel Processing Technology, vol. 88, no. 1, pp. 23–28, 2007.
View at: Publisher Site | Google Scholar
C. Li and K. Suzuki, “Resources, properties and utilization of tar,” Resources, Conservation and Recycling, vol. 54, no. 11, pp. 905–915, 2010.
View at: Publisher Site | Google Scholar
L. Li, K. Morishita, H. Mogi, K. Yamasaki, and T. Takarada, “Low-temperature gasification of a woody biomass under a nickel-loaded brown coal char,” Fuel Processing Technology, vol. 91, no. 8, pp. 889–894, 2010.
View at: Publisher Site | Google Scholar
L. Devi, K. J. Ptasinski, and F. J. J. G. Janssen, “A review of the primary measures for tar elimination in biomass gasification processes,” Biomass and Bioenergy, vol. 24, no. 2, pp. 125–140, 2002.
View at: Publisher Site | Google Scholar
J. Han and H. Kim, “The reduction and control technology of tar during biomass gasification/pyrolysis: an overview,” Renewable and Sustainable Energy Reviews, vol. 12, no. 2, pp. 397–416, 2008.
View at: Publisher Site | Google Scholar
A. V. Bridgwater, “The technical and economic feasibility of biomass gasification for power generation,” Fuel, vol. 74, no. 5, pp. 631–653, 1995.
View at: Publisher Site | Google Scholar
D. Velegol, M. Gautam, and A. Shamsi, “Catalytic cracking of a coal tar in a fluid bed reactor,” Powder Technology, vol. 93, no. 2, pp. 93–100, 1997.
View at: Publisher Site | Google Scholar
T. Kan, X. Sun, H. Wang, C. Li, and U. Muhammad, “Production of gasoline and diesel from coal tar via its catalytic hydrogenation in serial fixed beds,” Energy & Fuels, vol. 26, no. 6, pp. 3604–3611, 2012.
View at: Publisher Site | Google Scholar
T. Kan, H. Wang, H. He, C. Li, and S. Zhang, “Experimental study on two-stage catalytic hydroprocessing of middle-temperature coal tar to clean liquid fuels,” Fuel, vol. 90, no. 11, pp. 3404–3409, 2011.
View at: Publisher Site | Google Scholar
H. Wang, F. Dai, Z. Li, and C. Li, “Upgrading shale oil distillation to clean fuel by coupled hydrogenation and ring opening reaction of aromatics on W–Ni/γ-Al₂O₃ catalyst,” Energy and Fuels, vol. 29, no. 8, pp. 4902–4910, 2015.
View at: Publisher Site | Google Scholar
H.-Y. Wang, T.-T. Jiao, Z.-X. Li, C.-S. Li, S.-J. Zhang, and J.-L. Zhang, “Study on palm oil hydrogenation for clean fuel over Ni-Mo-W/γ-Al₂O₃-ZSM-5 catalyst,” Fuel Processing Technology, vol. 139, pp. 91–99, 2014.
View at: Publisher Site | Google Scholar
J. Shao, R. Yan, H. Chen, H. Yang, and D. H. Lee, “Catalytic effect of metal oxides on pyrolysis of sewage sludge,” Fuel Processing Technology, vol. 91, no. 9, pp. 1113–1118, 2010.
View at: Publisher Site | Google Scholar
P. Wang, L. Jin, J. Liu, S. Zhu, and H. Hu, “Analysis of coal tar derived from pyrolysis at different atmospheres,” Fuel, vol. 104, pp. 14–21, 2013.
View at: Publisher Site | Google Scholar
L. Yan, X. Kong, R. Zhao, F. Li, and K. Xie, “Catalytic upgrading of gaseous tars over zeolite catalysts during coal pyrolysis,” Fuel Processing Technology, vol. 138, pp. 424–429, 2015.
View at: Publisher Site | Google Scholar
G. Li, L. Yan, R. Zhao, and F. Li, “Improving aromatic hydrocarbons yield from coal pyrolysis volatile products over HZSM-5 and Mo-modified HZSM-5,” Fuel, vol. 130, pp. 154–159, 2014.
View at: Publisher Site | Google Scholar
J. Liu, H. Hu, L. Jin, P. Wang, and S. Zhu, “Integrated coal pyrolysis with CO2 reforming of methane over Ni/MgO catalyst for improving tar yield,” Fuel Processing Technology, vol. 91, no. 4, pp. 419–423, 2010.
View at: Publisher Site | Google Scholar
L. Jin, X. Zhou, X. He, and H. Hu, “Integrated coal pyrolysis with methane aromatization over Mo/HZSM-5 for improving tar yield,” Fuel, vol. 114, pp. 187–190, 2013.
View at: Publisher Site | Google Scholar
S. Li, J. Chen, T. Hao et al., “Pyrolysis of Huang Tu Miao coal over faujasite zeolite and supported transition metal catalysts,” Journal of Analytical and Applied Pyrolysis, vol. 102, pp. 161–169, 2013.
View at: Publisher Site | Google Scholar
Z. Ma, X. Ma, J. Luo, L. Xu, and F. Yang, “Catalytic hydropyrolysis of five Chinese coals,” Energy and Fuels, vol. 26, no. 1, pp. 511–517, 2012.
View at: Publisher Site | Google Scholar
W. Li, N. Wang, and B. Li, “Product analysis of catalytic multi-stage hydropyrolysis of lignite,” Fuel, vol. 82, no. 5, pp. 569–573, 2003.
View at: Publisher Site | Google Scholar
X. Zou, J. Yao, X. Yang, W. Song, and W. Lin, “Catalytic effects of metal chlorides on the pyrolysis of lignite,” Energy & Fuels, vol. 21, no. 2, pp. 619–624, 2007.
View at: Publisher Site | Google Scholar
W. Li, N. Wang, and B. Li, “Process analysis of catalytic multi-stage hydropyrolysis of lignite,” Fuel, vol. 81, no. 11-12, pp. 1491–1497, 2002.
View at: Publisher Site | Google Scholar
M. N. Amin, Y. Li, R. Razzaq, X. Lu, C. Li, and S. Zhang, “Pyrolysis of low rank coal by nickel based zeolite catalysts in the two-staged bed reactor,” Journal of Analytical and Applied Pyrolysis, vol. 118, pp. 54–62, 2016.
View at: Publisher Site | Google Scholar
D. I. Cliff, K. R. Doolan, J. C. Mackie, and R. J. Tyler, “Products from rapid heating of a brown coal in the temperature range 400–2300 °C,” Fuel, vol. 63, no. 3, pp. 394–400, 1984.
View at: Publisher Site | Google Scholar
R. J. Tyler, “Flash pyrolysis of coals. 1. Devolatilization of a Victorian brown coal in a small fluidized-bed reactor,” Fuel, vol. 58, no. 9, pp. 680–686, 1979.
View at: Publisher Site | Google Scholar
G. Duman, M. Pala, S. Ucar, and J. Yanik, “Two-step pyrolysis of safflower oil cake,” Journal of Analytical and Applied Pyrolysis, vol. 103, pp. 352–361, 2013.
View at: Publisher Site | Google Scholar
Z. Tingyu, Z. Shouyu, H. Jiejie, and W. Yang, “Effect of calcium oxide on pyrolysis of coal in a fluidized bed,” Fuel Processing Technology, vol. 64, no. 1, pp. 271–284, 2000.
View at: Publisher Site | Google Scholar

Copyright

Copyright © 2017 Muhammad Nadeem Amin et al. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

PDF Download Citation

Download other formats

Order printed copies

Views

2677

Downloads

1285

Citations