An Electrochemical Study to Evaluate the Effect of Calcium Nitrite Inhibitor to Mitigate the Corrosion of Reinforcement in Sodium Chloride Contaminated Ca(OH)2 Solution

Table 4

Electrochemical parameters were extracted after fitting of potentiodynamic plots in Tafel region.

[Cl/]Concentration of NaCl (g/L) (mV)Corrosion rate
Vs Ag/AgCl(µA/cm2)(kΩ⋅cm2)(µm/year)

0.00.99−3351.29111.1014.99
7.91−3502.94102.4534.16
0.30.99−2630.33217.773.83
7.91−3100.29154.193.37
0.60.99−2530.021259.660.24
7.91−3010.16230.691.86
1.20.99−2300.009892.590.10
7.91−2910.14272.861.63