A Combined TEM/STEM and Micromagnetic Study of the Anisotropic Nature of Grain Boundaries and Coercivity in Nd-Fe-B Magnets
Figure 5
(a) TEM BF showing the c-(Pr,Nd)2O3 GBj-1, also visible in Figure 4, and SAED images identify the phases; (b) EELS line scan over the GBj, low Fe content (≈5 at%), high RE, and O (ratio ≈ 2/3); : the oxygen content was corrected (from the measured value) due to surface oxidation of the TEM specimen.