Influence of Friction Stir Welding on Mechanical Properties of Butt Joints of AZ61 Magnesium Alloy
Table 4
Fracture locations of tensile specimens.
| Welding condition | Macrograph | Welding condition | Macrograph |
| 400 rpm 200 mm/min | | 600 rpm 300 mm/min | |
| 800 rpm 400 mm/min | | 1000 rpm 500 mm/min | |
| 600 rpm 200 mm/min | | 900 rpm 300 mm/min | |
| 1200 rpm 400 mm/min | | 1500 rpm 500 mm/min | |
|
|