Improvement of the Early-Age Compressive Strength, Water Permeability, and Sulfuric Acid Resistance of Scoria-Based Mortars/Concrete Using Limestone Filler
Figure 16
XRD of 28 days’ cured VS30LF15-based paste (E: ettringite; MS: Monosulfate; HC: hemicarboaluminate; MC: monocarboaluminate; CH: calcium hydroxide; CSH: calcium silicate hydrates; CASH: calcium aluminate silicate hydrates; CC: calcium carbonate).