Advances in Materials Science and Engineering
Volume 2017, Article ID 8789247, 10 pages
https://doi.org/10.1155/2017/8789247
Research Article

Aging Properties of Polyvinylidenefluoride-Coated Polyesters Used in Tensioned Membrane Structure: Effect of Loading Protocol and Environment

1State Key Laboratory for Geomechanics and Deep Underground Engineering, School of Mechanics and Civil Engineering, China University of Mining and Technology, Xuzhou 221116, China
2School of Mechanics and Civil Engineering, China University of Mining and Technology, Xuzhou 221116, China

Correspondence should be addressed to Yingying Zhang; moc.361@58gniygniygnahz

Received 5 March 2017; Accepted 12 April 2017; Published 17 May 2017

Academic Editor: Kohji Tashiro

Copyright © 2017 Yingying Zhang and Mingyue Zhang. This is an open access article distributed under the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.

Linked References

  1. Y. Li, Study and Applications on Mechanical Properties of Membrane Materials and Structures, Tongji University, Shanghai, China, 2007.
  2. B. Forster and M. Mollaert, “European Design Guide for Tensile Surface Structures,” Tensinet, 2004. View at Google Scholar
  3. Y. Y. Zhang, Q. L. Zhang, C. Z. Zhou, and Y. Zhou, “Mechanical properties of PTFE coated fabrics,” Journal of Reinforced Plastics and Composites, vol. 29, no. 24, pp. 3624–3630, 2010. View at Google Scholar
  4. B. N. Bridgens and M. J. S. Birchall, “Form and function: The significance of material properties in the design of tensile fabric structures,” Engineering Structure, vol. 44, pp. 1–12, 2012. View at Publisher · View at Google Scholar · View at Scopus
  5. P. D. Gosling, B. D. Bridgens, and L. Zhang, “Adoption of a reliability approach for membrane structure analysis,” Structural Safety, vol. 40, pp. 39–50, 2013. View at Publisher · View at Google Scholar
  6. B. L. Kuai, Weathering Properties of PVC Coated Membrane Material, Tongji University, Shanghai, China, 2013.
  7. X. D. Yang and X. Ding, “Progress of Study on the aging of PVC-coated membrane material,” Synthetic Materials Aging and Application, vol. 41, no. 2, pp. 44–54, 2012. View at Google Scholar
  8. R. Sallis, “High performance coated fafbric structural materials,” Journal of Industrial Textiles, vol. 14, no. 1, pp. 36–45, 1984. View at Publisher · View at Google Scholar · View at Scopus
  9. M. P. Ansell, C. A. S. Hill, and C. Allgood, “Architectural PTFE-coated glass fabrics-their structure and limitations,” Textile Research Journal, vol. 53, no. 11, pp. 692–700, 1983. View at Publisher · View at Google Scholar · View at Scopus
  10. W. F. Polfus, “Weathering of industrial fabrics (accelerated and natural),” Journal of Industrial Textiles, vol. 7, no. 1, pp. 58–62, 1977. View at Google Scholar
  11. U. Eichert, “Residual tensile and tear strength of coated industrial fabrics determined in long-time tests in natural weather conditions,” Journal of Industrial Textiles, vol. 23, no. 4, pp. 311–327, 1994. View at Publisher · View at Google Scholar · View at Scopus
  12. H. Toyada, S. Nireky, H. Jutunen, and T. Ohnuma, “Durability of PVC Coated Fabric for Membrane Structures,” I.A.S.S.S, 1990, Dresden and Cottbus. View at Google Scholar
  13. H. Toyada, H. Sakabe, T. Itoh, T. Konishi, and T. Torii, “Weatherability of Membrane Structure Materials as Determined by Exposure Conditions,” ESN 1 Gakkaishi, 1994. View at Google Scholar
  14. R. Levinson, P. Berdahl, A. A. Asefaw Berhe, and H. Akbari, “Effects of soiling and cleaning on the reflectance and solar heat gain of a light-colored roofing membrane,” Atmospheric Environment, vol. 39, no. 40, pp. 7807–7824, 2005. View at Publisher · View at Google Scholar · View at Scopus
  15. H. A. Razak, C. S. Chua, and H. Toyoda, “Weatherability of coated fabrics as roofing material in tropical environment,” Building and Environment, vol. 39, no. 1, pp. 87–92, 2004. View at Publisher · View at Google Scholar · View at Scopus
  16. K. Zerdzicki, P. Kłosowski, and K. Woznica, “Application of the Bodner—Partom constitutive equations for modelling the technical fabric Valmex used for the hanging roof of the Forest Opera in Sopot,” in Shell Structures: Theory and Applications, W. Pietraszkiewicz and J. Gorski, Eds., vol. 3, pp. 579–82, Taylor; Francis/Balkema, London, UK, 2014. View at Google Scholar
  17. M. P. Ansell, “The degradative effect of boiling water on polyester fibres in a PVC-coated fabric,” Journal of Industrial Textiles, vol. 14, no. 4, pp. 242–255, 1985. View at Publisher · View at Google Scholar · View at Scopus
  18. P. Mailler, G. Nemoz, and P. Hamelin, “Long Term Behavior Characterization of Coated Fabrics for Architecture Membrane under Biaxial Loading,” Journal of Industrial Textiles, vol. 27, pp. 323–333, 1997. View at Publisher · View at Google Scholar · View at Scopus
  19. H. F. Liu, J. Han, and Z. Y. Zou, “Study on the tensile properties of membrane structure material in ultraviolet radiation,” Journal of Zhejiang Science-Technology University, vol. 27, no. 1, pp. 26–30, 2009. View at Google Scholar
  20. W. C. Qiu, X. D. Yang, X. Ding, and C. Hu, “hoto-oxidation of PVC-coated membrane material,” Journal of Textile Researh, vol. 31, no. 12, pp. 33–38, 2010. View at Google Scholar
  21. W. J. Martin, W. J. Chin, and T. Nguyen, “Reciprocity law experiments in polymeric photo degradation: a critical review,” Progress in Organic Coatings, vol. 47, no. 3-4, pp. 292–311, 2003. View at Google Scholar
  22. J. Chin, N. T. Nguyen, D. Byrd, and J. Martin, “Validation of the reciprocity law for coating photodegradation,” Journal of Coatings Technology and Research, vol. 2, no. 7, pp. 499–508, 2005. View at Publisher · View at Google Scholar · View at Scopus
  23. Z. L. Tan, “Estimation of the aging resistance of membrane structure materials under thermal, humid and ultraviolet conditions,” Journal of Applied Polymer Science, 2008, Shanghai, China, Donghua University. View at Google Scholar
  24. F. J. Wang, Study on the Photo-Oxidation of PVC-Coated Membrane Material under Tensile Stresses, Donghua University, Shanghai, China, 2015.
  25. A. K. Sen, Coated Textiles: Principles and Applications, CRC Press, 2nd edition, 2007. View at Publisher · View at Google Scholar
  26. Y. Y. Zhang, Q. L. Zhang, B. L. Kuai, and K. Lei, “Experimental analysis of tensile behaviors of polytetrafluoroethylene-coated fabrics subjected to monotonous and cyclic loading,” Textile Research Journal, vol. 84, no. 3, pp. 231–245, 2014. View at Google Scholar
  27. Serge Ferrari Company, http://en.sergeferrari.com/corporate-en/precontraint-serge-ferrari-patented-technology/.
  28. Y. Y. Zhang, Q. L. Zhang, and H. L. Lv, “Mechanical properties of PVC coated fabrics processed with precontraint@ technology,” Journal of Reinforced Plastics and Composites, vol. 31, no. 23, pp. 1670–1684, 2012. View at Google Scholar
  29. A. Ambroziak, “Mechanical properties of Precontraint 1202S coated fabric under biaxial tensile test with different load ratios,” Construction and Building Materials, vol. 80, no. 1, pp. 210–224, 2015. View at Publisher · View at Google Scholar · View at Scopus
  30. A. Ambroziak, “Mechanical properties of polyester coated fabric subjected to biaxial loading,” Journal of Materials in Civil Engineering, vol. 27, no. 11, Article ID 04015012, 2015. View at Publisher · View at Google Scholar
  31. International Organization for Standardization. ISO 4892-2:2013, Plastics—Methods of exposure to laboratory light sources—Part 2: Xenon-arc lamps, 2013.
  32. DG/TJ08-2019-2007, “Inspection guidelines for membrane structures,” Shanghai, China.
  33. J. W. Chen and W. J. Chen, “Central Crack Tearing Testing of Laminated Fabric Uretek3216LV under Uniaxial and Biaxial Static Tensile Loads,” Journal of Materials in Civil Engineering, vol. 28, no. 7, Article ID 04016028, 2016. View at Publisher · View at Google Scholar
  34. H. L. Yi, X. Ding, and S. H. Chen, “Estimation of the elastic constants of architectural membrane under biaxial tensile loading,” Engineering Mechanics, vol. 23, no. 10, pp. 180–183, 2006. View at Google Scholar
  35. J. W. Chen, W. J. Chen, and D. X. Zhang, “Experimental study on uniaxial and biaxial tensile properties of coated fabric for airship envelopes,” Journal of Reinforced Plastics and Composites, vol. 33, no. 7, pp. 627–644, 2014. View at Publisher · View at Google Scholar · View at Scopus
  36. Z. R. Chen, B. L. Kuai, and Q. L. Zhang, “Experimental research on mechanical properties of PVC membrane after artificial accelerated aging,” Structural Engineer, vol. 32, no. 4, pp. 119–124, 2013. View at Google Scholar
  37. Z. R. Chen, Q. L. Zhang, and W. L. Xue, “Experimental research on mechanical properties of PVC membrane after aging,” IASS Symposium, 2013. View at Google Scholar
  38. Y. Y. Zhang, X. G. Song, Q. L. Zhang, and H. L. Lv, “Fracture failure analysis and strength criterion for PTFE-coated woven fabrics,” Journal of Composite Materials, vol. 49, no. 12, pp. 1409–1421, 2015. View at Google Scholar