Failure Modes in Concrete Repair Systems due to Ongoing Corrosion
Figure 11
Lattice simulation of corrosion induced cracking of experiments reported in [13] (a) in mortar (imposed internal pressure of 17.32 MPa) and in (b) SHCC (imposed internal pressure of 103.58 MPa).
(a) |