Fresh-State Properties of Mortars with Recycled Glass Aggregates: Global Unification of Behavior
Table 3
Results of the fresh-state properties of RGM.
| | Water needed for 1 dm3 (g) | Final /c ratio | Density (g/cm3) | Air content (%) ASTM C231 | Air content (%) ASTM C185 |
| UM-A | 327.35 | 0.68 | 2.18 | 2.0 | 0.2 | 15RGM-A | 314.63 | 0.70 | 2.02 | 8.3 | 7.0 | 30RGM-A | 300.14 | 0.71 | 1.87 | 13.7 | 13.1 | 60RGM-A | 297.70 | 0.81 | 1.63 | 22.1 | 22.3 | 100RGM-A | 278.39 | 0.93 | 1.57 | 22.3 | 22.6 |
| UM-B | 334.44 | 0.84 | 2.16 | 2.0 | 0.2 | 15RGM-B | 293.83 | 0.84 | 1.96 | 10.1 | 8.9 | 30RGM-B | 303.43 | 0.90 | 1.78 | 16.7 | 16.2 | 60RGM-B | 301.54 | 0.99 | 1.57 | 23.6 | 24.1 | 100RGM-B | 304.32 | 1.12 | 1.48 | 25.0 | 26.1 |
| UM-C | 334.28 | 0.98 | 2.15 | 1.8 | 0 | 15RGM-C | 316.49 | 0.99 | 1.91 | 11.7 | 10.4 | 30RGM-C | 286.15 | 1.01 | 1.77 | 17.4 | 16.8 | 60RGM-C | 302.84 | 1.15 | 1.59 | 22.4 | 22.7 | 100RGM-C | 327.67 | 1.40 | 1.50 | 22.9 | 23.8 |
|
|