Feasibility of Reduced Lap-Spliced Length in Polyethylene Fiber-Reinforced Strain-Hardening Cementitious Composite
Table 5
Experimental test results.
| Specimen ID | Initial cracking | Tensile strength (MPa) | Tensile strain (%) | Average crack width at 0.1% tensile strain (μm) | Average bond strength by (1) (MPa) | Strength (MPa) | Strain (%) |
| C40 | 95 | 0.008 | 316 | 0.06 | 89 | 2.69 | C80 | 149 | 0.002 | 168 | 0.06 | 214 | 2.72 | 40P40/00 | 125 | 0.003 | 375 | 0.83 | 43 | 7.67 | 40P40/10 | 235 | 0.002 | 391 | 1.78 | 14 | 8.10 | 40P80/00 | 89 | 0.005 | 316 | 2.13 | 47 | 11.80 | 40P80/10 | 196 | 0.002 | 321 | 0.50 | 49 | 10.76 | 60P40/00 | 73 | 0.005 | 491 | 0.18 | 43 | 8.24 | 60P40/10 | 124 | 0.001 | 506 | 0.20 | 25 | 7.76 | 60P80/00 | 89 | 0.003 | 401 | 0.14 | 34 | 11.54 | 60P80/10 | 240 | 0.002 | 428 | 0.07 | 29 | 13.76 |
|
|