The Mechanical Properties of a Novel STMR Damper Based on Magnetorheological Silly Putty
Table 3
, , , and
of the MRSP samples.
| Samples | Magnetic flux density, B (T) | (MPa) | (MPa) | (MPa) | (%) |
| MRSP 1 | 0 | 0.287 | 0.00346 | 0.28354 | 8194.80 | 0.102 | 0.349 | 0.01620 | 0.33280 | 2054.32 | 0.211 | 0.480 | 0.06410 | 0.41590 | 648.83 | 0.321 | 0.566 | 0.10900 | 0.45700 | 419.27 | 0.430 | 0.603 | 0.13400 | 0.46900 | 350 | 0.533 | 0.618 | 0.14400 | 0.47400 | 329.17 | 0.627 | 0.627 | 0.15000 | 0.47700 | 318 |
| MRSP 2 | 0 | 0.309 | 0.00531 | 0.30369 | 5719.21 | 0.102 | 0.383 | 0.03550 | 0.34750 | 978.87 | 0.211 | 0.873 | 0.22900 | 0.64400 | 281.22 | 0.321 | 1.060 | 0.37000 | 0.69000 | 186.49 | 0.430 | 1.160 | 0.44000 | 0.72000 | 163.64 | 0.533 | 1.190 | 0.45900 | 0.73100 | 159.26 | 0.627 | 1.200 | 0.47100 | 0.72900 | 154.78 |
| MRSP 3 | 0 | 0.411 | 0.0131 | 0.39790 | 3037.40 | 0.102 | 0.924 | 0.2900 | 0.63400 | 218.62 | 0.211 | 1.280 | 0.6690 | 0.61100 | 91.33 | 0.321 | 1.500 | 0.9190 | 0.58100 | 63.22 | 0.430 | 1.610 | 1.0400 | 0.57000 | 54.81 | 0.533 | 1.670 | 1.0900 | 0.58000 | 53.21 | 0.627 | 1.710 | 1.1300 | 0.58000 | 51.33 |
| MRSP 4 | 0 | 0.44 | 0.0228 | 0.41720 | 1829.82 | 0.102 | 1.24 | 0.366 | 0.87400 | 238.80 | 0.211 | 1.90 | 1.19 | 0.71 | 59.66 | 0.321 | 2.14 | 1.59 | 0.55 | 34.59 | 0.430 | 2.24 | 1.77 | 0.47 | 26.55 | 0.533 | 2.31 | 1.86 | 0.45 | 24.19 | 0.627 | 2.31 | 1.92 | 0.39 | 20.31 |
| MRSP 5 | 0 | 0.51 | 0.0239 | 0.4861 | 2033.89 | 0.102 | 1.67 | 0.814 | 0.8560 | 105.16 | 0.211 | 2.15 | 1.67 | 0.48 | 28.74 | 0.321 | 2.29 | 1.95 | 0.34 | 17.44 | 0.430 | 2.32 | 2.04 | 0.28 | 13.73 | 0.533 | 2.33 | 2.08 | 0.25 | 12.02 | 0.627 | 2.34 | 2.12 | 0.22 | 10.38 |
|
|