Behaviors of Oxide Film during Semisolid Brazing of SiC<sub>p</sub>/6063Al Composite Materials

<div>The microstructure of the as-rolled filler metal heated to different temperatures with compression between the SiC<sub>p</sub>/Al plates: (a<sub>1</sub>)–(d<sub>1</sub>) center region and (a<sub>2</sub>)–(d<sub>2</sub>) edge region of the filler metal heated to 382°C, 386°C, 392°C, and 410°C.</div>

Advances in Materials Science and Engineering

fig7

Figure 7

Figure 7: Behaviors of Oxide Film during Semisolid Brazing of SiC<sub>p</sub>/6063Al Composite Materials 

Advances in Materials Science and Engineering

Behaviors of Oxide Film during Semisolid Brazing of SiCp/6063Al Composite Materials

Figure 7

Behaviors of Oxide Film during Semisolid Brazing of SiC_p/6063Al Composite Materials