The Mechanical Behaviors of Various Dental Implant Materials under Fatigue
Table 1
The properties of materials used in this study.
| Material name | Density (g/cm3) | Young’s modulus (GPa) | Poisson’s ratio | Ultimate tensile strength (MPa) | Reference number |
| AISI 316L stainless steel | 8.00 | 192 | 0.30 | 860 | [27–29] | Nanoporous anodic alumina | 3.96 | 370 | 0.22 | 220 | [30, 31] | L-605 CoCr alloy | 9.24 | 240 | 0.29 | 1180 | [32] | cp Ti with the nanotubular TiO2 surface | 3.89 | 40 | 0.31 | 640 | [33, 34] | Yttrium-stabilized zirconia (YSZ) | 6.05 | 197 | 0.33 | 432 | [35–37] | Zirconia-toughened alumina (ZTA) | 4.10 | 310 | 0.26 | 760 (flexural) | [38] | Trabecular bone | — | 1.38 | 0.30 | — | [39] |
|
|