Joining of Cf/SiC Ceramic Matrix Composites: A Review
Table 5
Self-joining of Cf/SiC composites using inorganic filler (BS = bend strength).
| CMCs | Basic information | Joining material | Process parameters | Shear strength (MPa) | Ref. |
| Cf/SiC | 2D, CVI, 2.05 g/cm3, 40 MPa | Ti3SiC2 | 1600°C, 30 min, 20–40 MPa, Ar | 110.4 (BS) | [55] | Cf/SiC | 3D, CVI | PSZ | 1300°C, N2 | 29.6 | [64] | Cf/SiC | 3D, PIP, 1.9 g/cm3 | Si resin | 1400°C, 5 h, Ar | 3.51 | [57] | Cf/SiC | 2D, CVI, 1.7–2.2 g/cm3 | MoSi2/Si | 1450°C, 5 min, Ar | — | [58] |
|
|