Research Article
Electrochemical Reduction of Industrial Baths Used for Electropolishing of Stainless Steel
Table 2
Sample surface roughness in the area of noticed undulations.
| Type of bath | I (A·cm−2) | q/s (Amin·cm−2) | Sq (nm) | FFT_ampl | ΔZ (µm) | Surface defects after EP |
| Without ER | 0.20 | 9 | 547 | 547 | 15.50 | +++ | With ER | 0.20 | 9 | 645 | 645 | 9.68 | +++ | Without ER | 0.19 | 9 | 289 | 289 | 6.35 | ++ | Without ER | 0.18 | 9 | 170 | 170 | 2.32 | + | Without ER | 0.17 | 9 | 201 | 201 | 4.15 | None | Without ER | 0.05 | 9 | 271 | 271 | 2.31 | None | With ER | 0.05 | 9 | 218 | 218 | 4.33 | None |
|
|