Research Article
Effect of Ca Concentration on Microstructure and Mechanical Properties of As-Cast and As-Extruded Quasicrystal-Strengthened Mg-7.2Zn-2.4Gd Alloy
Table 1
EDS result of the as-cast alloys.
| Alloys | Point | Mg | Zn | Gd | Ca | Possible phase |
| Mg-7.2Zn-2.4Gd | 1 | 43.06 | 47.74 | 9.2 | — | I-phase | 2 | 78.79 | 17.95 | 3.26 | — | I-phase | 3 | 76.23 | 21.01 | 2.76 | — | I-phase + Mg4Zn7 |
| Mg-7.2Zn-2.4Gd-0.16Ca | 1 | 68.5 | 27.38 | 3.85 | 0.27 | I-phase + Mg4Zn7 | 2 | 77.56 | 19.84 | 0.14 | 2.46 | Mg6Zn3Ca2 + Mg4Zn7 | 3 | 60.18 | 33.38 | 6.43 | 0.01 | I-phase |
| Mg-7.2Zn-2.4Gd-0.32Ca | 1 | 94.28 | 4.50 | 0.84 | 0.38 | I-phase | 2 | 92.31 | 5.56 | 2.12 | 0.01 | W-phase | 3 | 98.89 | 0.92 | 0.07 | 0.12 | Mg6Zn3Ca2 + Mg4Zn7 |
| Mg-7.2Zn-2.4Gd-0.64Ca | 1 | 88.45 | 9.08 | 2.03 | 0.44 | W-phase + Mg6Zn3Ca2 | 2 | 82.85 | 11.58 | 5.44 | 0.12 | W-phase + Ca-containing phase | 3 | 87.51 | 8.56 | 3.81 | 0.12 | W-phase + Ca-containing phase | 4 | 77.69 | 15.20 | 6.95 | 0.16 | W-phase + Ca-containing phase |
|
|