Mechanical Recovery of Cracked Fiber-Reinforced Mortar Incorporating Crystalline Admixture, Expansive Agent, and Geomaterial
Table 3
Mechanical recovery indices for three mixes at 56 days of healing.
| Type | W (µm) | FCPL (kN) | Ploading (kN) | Punloading (kN) | Preloading (kN) | Kloading (MPa) | Kunloading (MPa) | Kreloading (MPa) | ISR | IDR |
| OPC-56D | 72 | 0.39 | 4.00 | 1.54 | 1.88 | 99 | 8.2 | 29 | 0.14 | 0.23 | 73 | 0.36 | 4.15 | 1.59 | 1.93 | 98 | 8.5 | 31 | 0.13 | 0.25 | 110 | 0.24 | 3.28 | 1.85 | 1.98 | 88 | 10.0 | 22 | 0.09 | 0.15 | 112 | 0.26 | 3.30 | 1.86 | 2.01 | 75 | 15.0 | 22 | 0.10 | 0.12 | 140 | 0.23 | 3.46 | 1.37 | 1.57 | 150 | 8.9 | 25 | 0.10 | 0.11 |
| SH1-56D | 82 | 0.46 | 3.23 | 1.10 | 1.51 | 117 | 8.7 | 42 | 0.19 | 0.31 | 91 | 0.48 | 3.41 | 1.36 | 1.81 | 136 | 13.0 | 54 | 0.22 | 0.33 | 107 | 0.33 | 3.13 | 1.21 | 1.56 | 104 | 6.9 | 29 | 0.18 | 0.23 | 110 | 0.35 | 3.11 | 1.72 | 1.84 | 84 | 9.5 | 25 | 0.09 | 0.21 | 142 | 0.21 | 3.46 | 1.28 | 1.53 | 98 | 6.8 | 23 | 0.11 | 0.18 | 147 | 0.18 | 2.73 | 1.20 | 1.36 | 91 | 6.2 | 18 | 0.10 | 0.14 |
| SH2-56D | 78 | 0.71 | 3.45 | 1.74 | 2.21 | 113 | 9.0 | 75 | 0.27 | 0.63 | 85 | 0.69 | 3.50 | 1.71 | 2.15 | 100 | 14 | 68 | 0.25 | 0.63 | 111 | 0.50 | 2.72 | 1.18 | 1.48 | 91 | 7.2 | 35 | 0.19 | 0.33 | 114 | 0.57 | 3.03 | 1.38 | 1.68 | 86 | 8.8 | 43 | 0.18 | 0.44 | 143 | 0.30 | 3.65 | 1.29 | 1.69 | 104 | 5.0 | 27 | 0.17 | 0.22 | 145 | 0.26 | 3.20 | 1.22 | 1.54 | 110 | 6.8 | 29 | 0.16 | 0.22 |
|
|