Research Article
The Effect of CuO on the Thermal Behavior of the High-Energy Combustion Agent of the Al/MnO2 System
Table 3
Enthalpy changes of five samples.
| Temperature (°C) | Enthalpy changes (kJ·mol−1) | Al + MnO2 | Al + MnO2 + CuO 5% | Al + MnO2 + CuO 10% | Al + MnO2 + CuO 15% | Al + MnO2 + CuO 20% |
| 0.000 | −967.169 | −959.215 | −949.999 | −940.838 | −931.153 | 100.000 | −968.541 | −960.606 | −951.405 | −942.261 | −932.596 | 200.000 | −969.443 | −961.541 | −952.367 | −943.253 | −933.622 | 300.000 | −969.746 | −961.894 | −952.766 | −943.700 | −934.122 | 400.000 | −969.678 | −961.892 | −952.824 | −943.823 | −934.314 | 500.000 | −969.648 | −961.935 | −952.935 | −944.004 | −934.570 | 600.000 | −969.820 | −962.181 | −953.250 | −944.392 | −935.034 | 700.000 | −993.139 | −985.068 | −975.677 | −966.364 | −956.553 | 800.000 | −989.230 | −981.473 | −972.388 | −963.387 | −953.891 | 900.000 | −988.859 | −981.190 | −972.188 | −963.273 | −953.868 | 1000.000 | −988.426 | −980.838 | −971.912 | −963.078 | −953.757 | 1100.000 | −984.414 | −975.420 | −965.160 | −954.958 | −944.270 | 1200.000 | −979.988 | −971.323 | −961.385 | −951.511 | −941.153 | 1300.000 | −957.449 | −956.577 | −954.114 | −951.881 | −949.157 | 1400.000 | −955.938 | −955.315 | −953.092 | −951.105 | −948.631 | 1500.000 | −954.477 | −954.097 | −952.106 | −950.359 | −948.127 |
|
|