Research Article
Prediction of Fatigue Life of Welded Joints Made of Fine-Grained Martensite-Bainitic S960QL Steel and Determination of Crack Origins
Table 5
Results of calculations of the strain range Δεnotch.
| Load εa (%) | Joint type | ΔσN (MPa) | Rσ (−) | (−) | αε (−) | ΔεN (%) | Δεnotch (%) |
| 0.15 | I | 611 | −0.02 | 0.616 | 2.09 | 0.278 | 0.58 | I | 618 | +0.03 | 0.651 | 2.16 | 0.281 | 0.61 | V | 579 | −0.19 | 0.500 | 1.74 | 0.264 | 0.46 | V | 622 | +0.33 | 0.953 | 2.51 | 0.283 | 0.71 |
| 0.20 | I | 826 | −0.09 | 0.780 | 2.41 | 0.376 | 0.91 | I | 841 | −0.11 | 0.778 | 2.40 | 0.383 | 0.92 | V | 890 | −0.135 | 0.805 | 2.22 | 0.405 | 0.90 | V | 800 | +0.13 | 0.944 | 2.49 | 0.364 | 0.91 |
| 0.25 | I | 1072 | −0.02 | 1.082 | 3.16 | 0.488 | 1.54 | I | 1090 | −0.21 | 0.925 | 2.74 | 0.496 | 1.36 | I | 1067 | −0.16 | 0.944 | 2.79 | 0.486 | 1.35 | V | 1068 | −0.17 | 0.937 | 2.48 | 0.486 | 1.20 | V | 956 | −0.14 | 0.861 | 2.32 | 0.435 | 1.01 |
| 0.30 | I | 1207 | −0.24 | 0.999 | 2.93 | 0.550 | 1.61 | I | 1219 | −0.40 | 0.894 | 2.66 | 0.555 | 1.48 | V | 1302 | −0.47 | 0.909 | 2.42 | 0.593 | 1.43 | V | 1248 | −0.41 | 0.909 | 2.42 | 0.568 | 1.37 |
| 0.40 | I | 1479 | −0.63 | 0.932 | 2.75 | 0.00673 | 1.85 | V | 1425 | −0.58 | 0.926 | 2.45 | 0.00649 | 1.59 | V | 1576 | −0.77 | 0.914 | 2.43 | 0.00718 | 1.74 |
|
|