Antiaging Property and Mechanism of Phase-Change Asphalt with PEG as an Additive
Table 3
Effects of different PEG dosage on antiaging properties of asphalt.
| | Index | PEG content (%) | 0 | 5 | 10 | 15 |
| Aging states | Unaged | Penetration (25°C, 100 g, 5 s) (0.1 mm) | 65 | 79 | 98 | 115 | Softening point (°C) | 53.0 | 48.5 | 49.0 | 53.0 | Ductility (5 cm/min, 15°C) (cm) | 150 | 135 | 119 | 107 | Viscosity (135°C, mPa·s) | 364 | 403 | 432 | 490 | RTFOT aged | Penetration (25°C, 100 g, 5 s) (0.1 mm) | 34 | 39 | 45 | 56 | Softening point (°C) | 55.0 | 50.5 | 50 | 55.5 | Ductility (5 cm/min, 15°C) (cm) | 13.7 | 12.7 | 15.4 | 11.3 | Viscosity (135°C, mPa·s) | 635 | 725 | 821 | 833 |
| Penetration ratio (%) | 52.3 | 52.4 | 53.9 | 52.7 | Ductility ratio (%) | 9.1 | 9.4 | 12.9 | 10.6 | Viscosity ratio () (%) | 1.7 | 1.8 | 1.9 | 1.7 | SP increment (°C) | 2 | 2 | 1 | 2.5 |
|
|